Cu对6082铝合金两级时效工艺的影响
来源期刊:上海金属2010年第5期
论文作者:杨丽丽 金曼 夏朝峰 王迎春
文章页码:39 - 42
关键词:Cu; 6082Al-Mg-Si合金; 两级时效; 三维原子探针; 硬度
Key words:Cu; 6082Al-Mg-Si Alloy; Two-Step Aging; 3DAP; Hardness
摘 要:采用三维原子探针研究了添加元素Cu对6082Al-Mg-Si合金两级时效过程中硬度变化的影响。研究结果表明:在先低温时效后T6时效的两级时效过程中,时效的第二阶段含Cu的6082Al-Mg-Si合金硬度始终高于不含Cu合金的硬度。在先高温时效后T6时效的两级时效过程中,含Cu的6082Al-Mg-Si合金硬度始终高于不含Cu合金的硬度。这是因为元素Cu促进了时效过程中团簇的形成,使合金在时效初期形成大量团簇。因此,元素Cu使合金中的强化相增多,合金的硬度提高。
Abstract: The effect of Cu addition on the hardness in two-step aging of 6082Al-Mg-Si alloy was investigated by three-dimensional atom probe(3DAP).The result showed that the hardness of 0.6%Cu 6082Al-Mg-Si alloy aged at 170 ℃(T6) after presaging at 50 ℃、70 ℃ or 110 ℃ become higher than that of 6082Al-Mg-Si alloy without Cu,the hardness of 0.6%Cu 6082Al-Mg-Si alloy aged at 170 ℃(T6) after presaging at 190 ℃ for 20 min、40 min or 60 min become higher than that of 6082Al-Mg-Si alloy without Cu.Because Cu element accelerated the clusters formation during aging process,the number of the precipitates increased.Therefore,the hardness of 6082Al-Mg-Si alloy with Cu element was enhanced.
基金信息:国家自然科学基金资助项目
杨丽丽1,金曼1,夏朝峰1,王迎春1
(1.上海市上海大学材料科学与工程学院)
摘 要:采用三维原子探针研究了添加元素Cu对6082Al-Mg-Si合金两级时效过程中硬度变化的影响。研究结果表明:在先低温时效后T6时效的两级时效过程中,时效的第二阶段含Cu的6082Al-Mg-Si合金硬度始终高于不含Cu合金的硬度。在先高温时效后T6时效的两级时效过程中,含Cu的6082Al-Mg-Si合金硬度始终高于不含Cu合金的硬度。这是因为元素Cu促进了时效过程中团簇的形成,使合金在时效初期形成大量团簇。因此,元素Cu使合金中的强化相增多,合金的硬度提高。
关键词:Cu; 6082Al-Mg-Si合金; 两级时效; 三维原子探针; 硬度