Al-(7.8~9.0)Zn-1.6Mg-(1.0~2.2)Cu合金铸态及其均匀化组织

来源期刊:中国有色金属学报2010年第9期

论文作者:万里 邓运来 张云崖 张新明

文章页码:1698 - 1704

关键词:Al-Zn-Mg-Cu合金;铸态;均匀化;微结构

Key words:Al-Zn-Mg-Cu alloy; as cast; homogenization; microstructure

摘    要:采用光学显微镜(OM)、X射线衍射(XRD)、差示扫描量热仪(DSC)和扫描电镜(SEM)及其附件能谱仪(EDX)研究Al-(7.8~9.0)Zn-1.6Mg-(1.0~2.2)Cu铝合金的铸态及其均匀化组织。结果表明: 该铝合金的铸态凝固组织由α(Al)基体+Mg(Zn, Al, Cu)2非平衡共晶相组成;铸态组织中粗大非平衡共晶组织的体积分数随着Zn含量的增加而增大,且伴随其周围析出的条状、细小Mg(Zn, Al, Cu)2粒子也逐渐增多、粗化;当Cu含量(质量分数)为1.0%、1.4%、2.2%时,铸态组织晶内的独立第二相分别为T(Al2Zn3Mg3)相、S(Al2CuMg)相、T(Al2Zn3Mg3)相+θ(Al2Cu)相;各成分合金经过(470 ℃, 24h)均匀化处理时,基体中仅剩下均匀化过程无法消除的尺寸较小、数量较少的初生富Fe相。

Abstract: The microstructures of the as-cast and homogenized Al-(7.8-9.0)Zn-1.6Mg-(1.0-2.2)Cu aluminum alloys were studied by OM, XRD, DSC, SEM and EDX techniques. The results show that the as-cast microstructure of Al-(7.8-9.0)Zn-1.6Mg-(1.0-2.2)Cu aluminum alloy mainly consists of Mg(Zn, Al, Cu)2 phase and α(Al) matrix. The volume fraction of coarse eutectic-structure increases with Zn content increasing. Meanwhile, the accompanying precipitations of small Mg(Zn, Al, Cu)2 particles are also gradually increased. When Cu content(mass fraction) is 1.0%, 1.4% and 2.2% , the main second phases within grains are T(Al2Zn3Mg3) phase, S(Al2CuMg) phase and T(Al2Zn3Mg3)+ θ(Al2Cu) phases, respectively. The only remained particles in the matrix are some small Fe-rich particles after being homogenized at 470 ℃ for 24 h.



详情信息展示

文章编号:1004-0609(2010)09-1698-07

Al-(7.8~9.0)Zn-1.6Mg-(1.0~2.2)Cu合金

铸态及其均匀化组织

万  里1, 2, 邓运来1, 2, 张云崖1, 2, 张新明1, 2

(1. 中南大学 材料科学与工程学院,长沙 410083;

2. 中南大学 有色金属材料科学与工程教育部重点实验室,长沙 410083)

摘  要:采用光学显微镜(OM)、X射线衍射(XRD)、差示扫描量热仪(DSC)和扫描电镜(SEM)及其附件能谱仪(EDX)研究Al-(7.8~9.0)Zn-1.6Mg-(1.0~2.2)Cu铝合金的铸态及其均匀化组织。结果表明: 该铝合金的铸态凝固组织由α(Al)基体+Mg(Zn, Al, Cu)2非平衡共晶相组成;铸态组织中粗大非平衡共晶组织的体积分数随着Zn含量的增加而增大,且伴随其周围析出的条状、细小Mg(Zn, Al, Cu)2粒子也逐渐增多、粗化;当Cu含量(质量分数)为1.0%、1.4%、2.2%时,铸态组织晶内的独立第二相分别为T(Al2Zn3Mg3)相、S(Al2CuMg)相、T(Al2Zn3Mg3)相+θ(Al2Cu)相;各成分合金经过(470 ℃, 24h)均匀化处理时,基体中仅剩下均匀化过程无法消除的尺寸较小、数量较少的初生富Fe相。

关键词:Al-Zn-Mg-Cu合金;铸态;均匀化;微结构

中图分类号:TG249.9       文献标志码:A

Microstructures of as-cast and homogenized

Al-(7.8-9.0)Zn-1.6Mg-(1.0-2.2)Cu aluminum alloys

WAN Li1, 2, DENG Yun-lai1, 2, ZHANG Yun-ya1, 2, ZHANG Xin-ming1, 2

 (1. School of Materials Science and Engineering, Central South University, Changsha 410083, China;

2. Key Laboratory of Nonferrous Metal Materials Science and Engineering, Ministry of Education,

Central South University, Changsha 410083, China)

Abstract: The microstructures of the as-cast and homogenized Al-(7.8-9.0)Zn-1.6Mg-(1.0-2.2)Cu aluminum alloys were studied by OM, XRD, DSC, SEM and EDX techniques. The results show that the as-cast microstructure of Al-(7.8-9.0)Zn-1.6Mg-(1.0-2.2)Cu aluminum alloy mainly consists of Mg(Zn, Al, Cu)2 phase and α(Al) matrix. The volume fraction of coarse eutectic-structure increases with Zn content increasing. Meanwhile, the accompanying precipitations of small Mg(Zn, Al, Cu)2 particles are also gradually increased. When Cu content(mass fraction) is 1.0%, 1.4% and 2.2% , the main second phases within grains are T(Al2Zn3Mg3) phase, S(Al2CuMg) phase and T(Al2Zn3Mg3)+ θ(Al2Cu) phases, respectively. The only remained particles in the matrix are some small Fe-rich particles after being homogenized at 470 ℃ for 24 h.

Key words: Al-Zn-Mg-Cu alloy; as cast; homogenization; microstructure

                    


7xxx系铝合金凭借其优越的力学性能被航空航天等制造领域作为主要的结构材料[1-3] 。而这些性能往往决定于合金材料基体中第二相的种类、数量、分布等存在状态。如粗大(>1 μm)的S相(Al2CuMg)、富Fe相等粒子在基体中的大量存在将使7xxx系铝合金的力学性能大大恶化[4-8] 。因此如何在合金设计时对合金成分进行合理的调控以及在随后的热处理过程中对热处理工艺的合理制定和优化就显得非常的重要,如提高合金中的Zn/Mg将使合金的强度得到大大提高,但其抗应力腐蚀和剥落腐蚀的能力会随之下降[9],在高压下均匀化有助于难溶第二相粒子的回溶[10],采用合理的固溶制度将有利于提高7xxx铝合金的淬透层深度,从而大大提高厚板的整体性能[11]等。而这些设计原理的出发点又与合金材料在铸造过程中第二相的析出情况以及其在均匀化或固溶过程中的演变规律息息相关。也就是说要针对不同的基体组织采用不同的热处理工艺才能使材料得到理想的性能。

已有不少文献报道了不同合金元素的添加将使凝固组织中存在的第二相的种类及数量不同[12-13] ,但是所得结论说法不一,也不系统。因此,本文作者针对高断裂韧性和低淬透性的新一代超高强AA7085铝合金[14-15],较系统地研究主成分Cu、Zn波动对合金凝固组织及其均匀化制度的影响,以期为高性能7085型及类7085型铝合金的制备提供实验依据。

1  实验

实验室采用高纯铝、纯锌、纯镁和铝-铜、铝-锆中间合金配料,晶粒细化剂为Al-5Ti-B。在石墨坩埚电阻炉内进行熔炼,熔炼温度为750~780 ℃,精炼温度为730~750 ℃,铸造温度为710~720 ℃,除气剂采用C2Cl6。将熔体浇铸于铁模中获得6种不同成分的铝合金方锭,其尺寸为30 mm×80 mm×120 mm,其化学成分如表1所列,其中合金试样B、C在文献[15]报道的AA7085铝合金成分范围,属于7085型铝合金,合金试样A、D、E、F分别为Cu含量或Zn含量在合金C成分基础上下波动的类7085型铝合金。采用NET2SCH-200 F3热分析对各合金成分的非平衡共晶温度进行示差扫描量热(DSC)分析。结果表明,在升温速度为10 ℃/min的条件下,6种铝合金的第一级均匀化的温度均不宜超过475 ℃,因此,本研究对6种合金的均匀化制度最终确定为(470 ℃, 24 h)。

表1  实验研究铝合金的名义成分

Table 1  Nominal composition of investigated aluminum alloys (mass fraction, %)

试样在XJP-6A型金相显微镜上进行光学金相观察观察,金相试样的腐蚀试剂为1 mL HF+16 mL HNO3+3g CrO3 + 83 mL蒸馏水(Graff sargent试剂)。用JSM-6360LV扫描电镜及其能谱仪(EDS)附件对试样进行微结构分析。X射线衍射(XRD)物相分析采用Rigaku D/Max 2500型18KW转靶X射线衍射仪。

2  结果与讨论

2.1  铸态试样的微结构分析

图1所示为6种合金成分试样铸态组织的典型金相照片。从图1可以看出,对于仅Cu含量不同的4种合金试样A、B、C、D,随着Cu含量的增加,铸态晶粒组织逐渐细化,且细化效果十分显著,其晶粒尺寸从100 μm减小到50 μm左右。与此同时,其晶界尺寸逐渐粗化。这与MONDAL等[12]研究时发现的增加Cu和Mg可使7055合金晶粒细化的现象十分相似。这是因为在试样凝固形核过程中,增加合金元素含量更容易引起合金成分起伏,有利于形成更多能够稳定存在并长大的有效非均匀形核质点;同时,在凝固过程中形成的大量第二相质点能够有效地阻碍晶粒长大时所必需的晶界迁移。在凝固过程中,溶质分配系数k<1的合金元素如Zn、Mg、Cu等倾向于在晶界和枝晶边界集中形成晶内偏析,因而图1中合金试样C、D、E、F的晶界与合金试样A、B的晶界相比,呈现明显宽化的现象。

铸态合金中典型成分试样的XRD谱如图2所示。从图2可以看出,4种合金试样基体中存在相同种类的第二相,即使Cu含量最高的合金试样D经过极端的1(?)/min的慢扫描检测,其结果显示基体中除了Al和MgZn2相以外,也没有其他新相存在。同时,根据图2可以判断,图1中晶界处的物质为MgZn2晶体结构的非平衡共晶组织。