Dynamic response and plastic deformation behavior of Ti–5Al–2.5Sn ELI and Ti–8Al–1Mo–1V alloys under high-strain rate
来源期刊：Rare Metals2014年第2期
论文作者：Yan-Ling Wang Song-Xiao Hui Rui Liu Wen-Jun Ye Yang Yu Ravil Kayumov
文章页码：127 - 133
摘 要：Split Hopkinson pressure bar test system was used to investigate the plastic deformation behavior and dynamic response character of a-type Ti–5Al–2.5Sn ELI and near a-type Ti–8Al–1Mo–1V titanium alloy when subjected to dynamic loading. In the present work, stress–strain curves at strain rate from 1.5 9 103to 5.0 9 103s-1were analyzed, and optical microscope（OM） was used to reveal adiabatic shearing behavior of recovered samples. Results show that both the two alloys manifest significant strain hardening effects. Critical damage strain rate of the two alloys is about 4.3 9 103s-1, under which the impact absorbs energy of Ti–5Al–2.5Sn ELI and Ti–8Al–1Mo–1V are 560 and 470 MJ m-3, respectively. Both of them fracture along the maximum shearing strength orientation, an angle of 45° to the compression axis. No adiabatic shear band（ASB） is found in Ti–5Al–2.5Sn ELI alloy, whereas several ASBs with different widths exist without regular direction in Ti–8Al–1Mo–1V alloy.
Yan-Ling Wang1，Song-Xiao Hui1，Rui Liu1，Wen-Jun Ye1，Yang Yu1，Ravil Kayumov2
1. State Key Laboratory for Fabrication & Processing of Nonferrous Metals, General Research Institute for Nonferrous Metals2. Department of Mechanical Engineering, Sun Moon University
摘 要：Split Hopkinson pressure bar test system was used to investigate the plastic deformation behavior and dynamic response character of a-type Ti–5Al–2.5Sn ELI and near a-type Ti–8Al–1Mo–1V titanium alloy when subjected to dynamic loading. In the present work, stress–strain curves at strain rate from 1.5 9 103to 5.0 9 103s-1were analyzed, and optical microscope（OM） was used to reveal adiabatic shearing behavior of recovered samples. Results show that both the two alloys manifest significant strain hardening effects. Critical damage strain rate of the two alloys is about 4.3 9 103s-1, under which the impact absorbs energy of Ti–5Al–2.5Sn ELI and Ti–8Al–1Mo–1V are 560 and 470 MJ m-3, respectively. Both of them fracture along the maximum shearing strength orientation, an angle of 45° to the compression axis. No adiabatic shear band（ASB） is found in Ti–5Al–2.5Sn ELI alloy, whereas several ASBs with different widths exist without regular direction in Ti–8Al–1Mo–1V alloy.