Characterization of NbSi2–Al2O3 nanocomposite coatings prepared with plasma spraying mechanically alloyed powders
来源期刊：International Journal of Minerals Metallurgy and Materials2015年第7期
论文作者：Zohreh Yazdani Fathallah Karimzadeh Mohammad-Hasan Abbasi Abbas Amini
文章页码：748 - 754
摘 要：The present study characterized NbS i2–Al2O3 nanocomposite powders plasma-sprayed on Ti–6Al–4Vsubstrates. The powders were agglomerated to obtain suitable particle sizes for spraying. The agglomerated powders were then plasma-sprayed using atmospheric plasma spraying. The structural transformations of the powders along with the morphological and mechanical changes of the coatings were examined by X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy, and hardness testing. The results showed that after plasma spraying, the grain size increased, and the lattice strain decreased. However, the grain size of this compound after spraying was still in the nanometer range. The coating was uniform and exhibited good adhesion to the substrate. The microhardness and fracture toughness of the nanocomposite coating were higher than those of a nanostructured NbS i2 coating.
Zohreh Yazdani，Fathallah Karimzadeh，Mohammad-Hasan Abbasi，Abbas Amini
Department of Materials Engineering, Isfahan University of Technology
摘 要：The present study characterized NbS i2–Al2O3 nanocomposite powders plasma-sprayed on Ti–6Al–4Vsubstrates. The powders were agglomerated to obtain suitable particle sizes for spraying. The agglomerated powders were then plasma-sprayed using atmospheric plasma spraying. The structural transformations of the powders along with the morphological and mechanical changes of the coatings were examined by X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy, and hardness testing. The results showed that after plasma spraying, the grain size increased, and the lattice strain decreased. However, the grain size of this compound after spraying was still in the nanometer range. The coating was uniform and exhibited good adhesion to the substrate. The microhardness and fracture toughness of the nanocomposite coating were higher than those of a nanostructured NbS i2 coating.