Microstructural evolution and stress state related to mechanical properties of electron beam melted Ti-6Al-4V alloy modi?ed by laser shock peening
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第15期
论文作者：Liang Lan Xinyuan Jin Shuang Gao Bo He Yonghua Rong
文章页码：153 - 161
摘 要：This work characterizes microstructural evolutions of electron beam melted（EBM） Ti-6 Al-4 V alloy modified via laser shock peening（LSP）.The depth stress distribution and tensile properties of EBM Ti-6 Al-4 V alloy were measured before and after LSP.The results indicate that microstructure consists of β phase with 7.2%±0.4% vol.% and balance α lamellar in EBM sample,and the α lamella was refined into nano-equiaxed grains and submicro-equiaxed grains after LSP.The dominant refinement mechanism is revealed during LSP.Stacking faults were found in the LSP-treated sample,and their corresponding planes were determined as（0001） basal plane,（1010） prismatic plane,and（1011） pyramidal plane obtained by high resolution transmission electron microscopy.The subgrains and high-angle grains formed during dynamic recrystallization were identified by selected area electron diffraction pattern.The LSP treatment produces a significantly residual compressive stress approximately-380 MPa with the depth of compressive stress layer reaching 450 μm.Strength and elongation of the EBM sample were significantly increased after LSP.The strength and ductility enhancements are attributed to compre s sive stress,grain refinement and grain gradient distribution of α phase.
Liang Lan1，Xinyuan Jin1，Shuang Gao1，Bo He1，Yonghua Rong2
1. Research Center of High-temperature Alloy Precision Forming, School of Material Engineering, Shanghai University of Engineering Science2. School of Materials Science and Engineering, Shanghai Jiao Tong University
摘 要：This work characterizes microstructural evolutions of electron beam melted（EBM） Ti-6 Al-4 V alloy modified via laser shock peening（LSP）.The depth stress distribution and tensile properties of EBM Ti-6 Al-4 V alloy were measured before and after LSP.The results indicate that microstructure consists of β phase with 7.2%±0.4% vol.% and balance α lamellar in EBM sample,and the α lamella was refined into nano-equiaxed grains and submicro-equiaxed grains after LSP.The dominant refinement mechanism is revealed during LSP.Stacking faults were found in the LSP-treated sample,and their corresponding planes were determined as（0001） basal plane,（1010） prismatic plane,and（1011） pyramidal plane obtained by high resolution transmission electron microscopy.The subgrains and high-angle grains formed during dynamic recrystallization were identified by selected area electron diffraction pattern.The LSP treatment produces a significantly residual compressive stress approximately-380 MPa with the depth of compressive stress layer reaching 450 μm.Strength and elongation of the EBM sample were significantly increased after LSP.The strength and ductility enhancements are attributed to compre s sive stress,grain refinement and grain gradient distribution of α phase.