The effect of multilayer structure on magnetic properties of FePt thin films
来源期刊：Acta Metallurgica Sinica2009年第1期
论文作者：Xiaomin CHENG Kaifeng DONG Xiaofei YANG Weiming CHENG Junbing YAN
Key words：L10-FePt thin films; Multilayer structure; Coercivity; Ordering temperature;
Abstract: The Fe/Pt multilayer films with different structures were deposited by RF magnetron sputtering on glass substrates, and the L10-FePt films were obtained after the as- deposited samples were subjected to vacuum annealing at various temperatures. Re-sults show that the Fe/Pt multilayer structure can effectively reduce the ordering temperature of FePt film, and the in-plane coercivity of [Fe (5.2 nm)/Pt (5.2 nm)]τmultilayers can reach 161.2 kA/m after annealed at 350 °C for 30 rain. When Fe and Pt layer thickness is equal, the coercivity of the film is the largest. On the other hand, the different Fe-Pt crystalline phases such as Fe3Pt and FePt3 phases are formed after annealing when the thickness ratio of Fe/Pt deviates from 1 after annealing. When Fe and Pt have the same thickness, the thinner single layer gets the lower ordering temperature and the larger coercivity.
Xiaomin CHENG1，Kaifeng DONG1，Xiaofei YANG1，Weiming CHENG1，Junbing YAN1
(1.Department of Electronic Science & Technology,Huazhong University of Science & Technology,Wuhan 430074,China)
Abstract:The Fe/Pt multilayer films with different structures were deposited by RF magnetron sputtering on glass substrates, and the L10-FePt films were obtained after the as- deposited samples were subjected to vacuum annealing at various temperatures. Re-sults show that the Fe/Pt multilayer structure can effectively reduce the ordering temperature of FePt film, and the in-plane coercivity of [Fe (5.2 nm)/Pt (5.2 nm)]τmultilayers can reach 161.2 kA/m after annealed at 350 °C for 30 rain. When Fe and Pt layer thickness is equal, the coercivity of the film is the largest. On the other hand, the different Fe-Pt crystalline phases such as Fe3Pt and FePt3 phases are formed after annealing when the thickness ratio of Fe/Pt deviates from 1 after annealing. When Fe and Pt have the same thickness, the thinner single layer gets the lower ordering temperature and the larger coercivity.
Key words:L10-FePt thin films; Multilayer structure; Coercivity; Ordering temperature;