简介概要

Transformation and dissolution of second phases during solution treatment of an Al-Zn-Mg-Cu alloy containing high zinc

来源期刊：Rare Metals2018年第5期

论文作者：Kai Wen Bai-Qing Xiong Yun-Qiang Fan Yong-An Zhang Zhi-Hui Li Xi-Wu Li Feng Wang Hong-Wei Liu

文章页码：376 - 380

摘要：The transformation and dissolution of Mg（Zn,Cu, Al）₂ phase during solution treatment of an Al-Zn-MgCu alloy containing high zinc were investigated by means of optical microscopy（OM）, scanning electron microscopy（SEM）, energy-dispersive X-ray spectrometry（EDX） and X-ray diffraction（XRD）. The results show that solution temperature is the main factor influencing phase dissolution. With solution temperature increasing, the content of residual phases decreases. Phase transformation from Mg（Zn, Cu, Al）2 to S（Al₂ CuMg） occurs under solution temperature of 450,460 and 465 ℃. Mg（Zn,Cu,Al）₂ phase is directly dissolved into the matrix under solution temperature of 470 and 475 ℃,and no S（Al₂ CuMg） phase transformed from Mg（Zn, Cu, Al）₂ phase is observed. The formation of S（Al₂ CuMg） phase is mainly controlled by Zn elemental diffusion. The mechanism of transformation and dissolution of second phases was investigated. At low temperature, the dissolution of Zn is faster than that of Mg and Cu, resulting in an appropriate condition to form S（Al₂ CuMg） phase. At high temperature, the dissolution of main alloying elements has no significant barrier among them to form S（Al₂ CuMg） phase.

稀有金属(英文版) 2018,37(05),376-380

Transformation and dissolution of second phases during solution treatment of an Al-Zn-Mg-Cu alloy containing high zinc

Kai Wen Bai-Qing Xiong Yun-Qiang Fan Yong-An Zhang Zhi-Hui Li Xi-Wu Li Feng Wang Hong-Wei Liu

State Key Laboratory of Nonferrous Metals and Processes,General Research Institute for Nonferrous Metals

收稿日期：11 June 2015

基金：financially supported by the National Program on Key Basic Research Project of China (No. 2012CB619504);National Natural Science Foundation of China (No. 51274046);

Transformation and dissolution of second phases during solution treatment of an Al-Zn-Mg-Cu alloy containing high zinc

Kai Wen Bai-Qing Xiong Yun-Qiang Fan Yong-An Zhang Zhi-Hui Li Xi-Wu Li Feng Wang Hong-Wei Liu

State Key Laboratory of Nonferrous Metals and Processes,General Research Institute for Nonferrous Metals

Abstract：

The transformation and dissolution of Mg(Zn,Cu, Al)₂ phase during solution treatment of an Al-Zn-MgCu alloy containing high zinc were investigated by means of optical microscopy(OM), scanning electron microscopy(SEM), energy-dispersive X-ray spectrometry(EDX) and X-ray diffraction(XRD). The results show that solution temperature is the main factor influencing phase dissolution. With solution temperature increasing, the content of residual phases decreases. Phase transformation from Mg(Zn, Cu, Al)2 to S(Al₂ CuMg) occurs under solution temperature of 450,460 and 465 ℃. Mg(Zn,Cu,Al)₂ phase is directly dissolved into the matrix under solution temperature of 470 and 475 ℃,and no S(Al₂ CuMg) phase transformed from Mg(Zn, Cu, Al)₂ phase is observed. The formation of S(Al₂ CuMg) phase is mainly controlled by Zn elemental diffusion. The mechanism of transformation and dissolution of second phases was investigated. At low temperature, the dissolution of Zn is faster than that of Mg and Cu, resulting in an appropriate condition to form S(Al₂ CuMg) phase. At high temperature, the dissolution of main alloying elements has no significant barrier among them to form S(Al₂ CuMg) phase.

Keyword：

Al-Zn-Mg-Cu alloy; Microstructure; Solution treatment; Phase transformation;

Author： Bai-Qing Xiong,e-mail:xiongbq@grinm.com;

Received： 11 June 2015

1 Introduction

Al-Zn-Mg-Cu alloy plates are widely used in the aeronautical and aerospace industries in consideration of a good combination of specific strength,hot workability,toughness and fatigue durability [ 1, 2] .Although the properties of Al-Zn-Mg-Cu alloys are very attractive,the processing of these alloys is quite difficult due to their high alloying element contents.The properties of these alloy plates can be optimized by applying a series of treatments,including solution,quenching and aging heat-treatments [ 3, 4] .Generally,the solution treatment is a primary and key step [ 5, 6, 7] .During the solution treatment,soluble phases can be re-dissolved into the matrix to form supersaturated solid solution,preparing for subsequent aging treatment.At a higher solution temperature,soluble phases can re-dissolve more sufficiently.However,for the single-stage solution treatment,the solution temperature should be below the incipient melting point for Mg(Zn,Cu,Al)2 phase.Otherwise,the alloy may be over-burnt,which is detrimental to mechanical performance.Besides,a solution process at high temperatures led to severe recrystallization and a decrease in the strength,toughness and even a resistance to corrosion of the aged materials [ 8, 9, 10] .Hence,to avoid severe recrystallization and get good overall performance after aging treatments,a preferential solution treatment regime should choose relatively low temperature on the basis of ensuring the re-dissolution of soluble phase.

Previous literatures chiefly focused on the adjustment of process temperature and time period to get superior micro structure and simply described phase species in alloys after solution treatment.Mazibuko and Curle [ 11] found that S(Al₂CuMg) phase occurred after solution treatment at 473℃.Deng et al. [ 6] also found that the specimen contained Al₂CuMg particles for temperature up to 475°C.On the other hand,Han et al. [ 7] asserted that the Mg(Zn,Cu,Al)2 phase directly dissolved into the matrix during solution treatment and no S(Al₂CuMg) phase was found.Apparently,the mechanism of phase dissolution or transition during solution treatment has received little attention.Hence,it is obliged to systemic ally clarify them.

In this paper,the transformation and dissolution of the second phases during solution treatment under various temperature regimes were studied.The present study was focused on the effect of the gap between Zn and Cu elemental diffusion rate on the Mg(Zn,Cu,Al)2 phase dissolution and its transition during solution treatment.The results could give indispensable information for optimizing the solution processing parameters.

2 Experimental

The present study was carried out on the 25-mm-thick hot extruded Al-Zn-Mg-Cu alloy plate with chemical composition of Al-8.02Zn-1.80Mg-2.02Cu-0.15Zr-0.046Fe(wt%).Solution treatments were conducted in air using a resistance-heated box furnace with forced air convection.The solution treatment procedures are listed in Table 1.The samples for metallographic observation were prepared through a conventional mechanical polishing and followed by etching with Graff Seagent solution (1 ml HF,16 ml HNO₃,3 g CrO₃ and 83 ml water).The metallographic observation was performed on optical microscopy (OM,Zeiss Axiovert 200 MAT).The morphology of the residual phase was examined on a scanning electron microscope(SEM,JEOL JSM 7001F).The second-phase particles were identified by energy-dispersive X-ray spectrometry(EDX).To quantitatively evaluate the dissolution of constituent particles,SEM images were taken at least ten random sites for each sample.By using Image-Pro Plus software,the content of remaining constituents in as-extruded and different solution-treated samples was determined.The microstructural characterization was carried out by X-ray diffractometer (XRD,Rigaku D/Max 2500)with 0.5°step.The content of the second-phase particles was measured on the SEM micrographs by using point counting with a grid containing 900 points [ 12] .The conductivity of the alloy at different conditions was measured by a WD-Z eddy current conductivity meter with at least five random sites for each sample.

下载原图

Table 1 Solution treatment schedules of as-extruded plate of Al-Zn-Mg-Cu alloy

3 Results and discussion

3.1 Observation of as-extruded microstructure

The micros tructures of as-extruded Al-Zn-Mg-Cu alloy plate are shown in Fig.1.It can be observed that a number of coarse second-phase particles distribute along the extruding direction.The EDS analysis reveals that these second particles are Mg(Zn,Cu,Al)2 phase and Fe-rich phase (Table 2).Large amounts of fine white phase are distributed homogenously in the matrix (Fig.1b).According to the EDS results,they are also Mg(Zn,Cu,Al)₂ phases.The XRD pattern of as-extruded Al-Zn-MgCu alloy (Fig.2) also proves that the primary phases areα(Al) and the phases with crystal structure of MgZn₂.Most second-phase particles are expected to be dissolved into the matrix by the solution treatment.However,the high temperature of the solution treatment inevitably increases recrystallization proportion.Therefore,it is necessary to optimize the solution treatment.

Fig.1 Morphologies of second-phase particles of as-extruded alloy:a OM image,b SEM image on longitudinal plane,and c high-magnitude SEM image on longitudinal plane with phases labeled by EDS.L,LT and ST being longitudinal direction,long-transverse direction and short-transverse direction,respectively

下载原图

Table 2 EDX results of second-phase particles of as-extruded plate from Fig.1 (at%)

Fig.2 XRD pattern of as-extruded alloy

3.2 Dissolution of constituent particles

The typical micrographs of the alloy after solution treatment at different conditions are shown in Fig.3.The corresponding EDS analysis is shown in Table 3.The S(Al₂CuMg) phase is observed in Samples SHT450,SHT460 and SHT465 (Points A,C,E,F and G in Fig.3).According to the contrast of different phases of SEMimages,few Mg(Zn,Cu,Al)2 phases still remain in Samples SHT450 and SHT460 (Points B,D in Fig.3).No(Al₂CuMg) phase is detected in as-extruded sample.Hence,it can be explained that S(Al₂CuMg) phase transforms from Mg(Zn,Cu,Al)2 phase during solution treatments.This is in agreement with literatures on solution treatments [ 13] .Only Fe-rich phase is observed in the microstructure of Samples SHT470 and SHT475.It is necessary to note that Fe-rich phase is also observed in Samples SHT450,SHT460 and SHT465,which is just not marked in the micrographs.To get a better view,the phase existence of samples solution-treated in different conditions is shown in Table 4.Various phases are labeled as“Y”for the existence and"N"for the inexistence.It can be obviously seen from the micrographs that the SHT samples treated at high temperatures possess less residual phases.In general,compared to the as-extruded alloy plate,the fine secondary phase particles are dissolved into the matrix of SHT samples.

Fig.3 SEM images of as-extruded alloy after solution-treated at different conditions:a,b SHT450;c,d SHT460;e,f SHT465;g,h SHT470;and i,j SHT475

The conductivity of the alloy at different conditions was also measured,as shown in Fig.4.Typically,the conductivity is used to indicate the supersaturation level of alloys.Compared to the as-extruded samples,the conductivity of the SHT samples exhibits a significant decrement.Besides,the conductivity decreases with the solution temperature increasing for Samples SHT450,SHT460,SHT465 and SHT470.That means a sustainable increment of the supers aturation of the matrix,namely the second-phase dissolution,occurs all the time.This is in accordance with the SEM observation.For Sample SHT475,the conductivity is higher than that of Sample SHT470.This can be explained that an increment of solution temperature is not beneficial to the supersaturation of the matrix,which means that an enhanced temperature is not necessary for phase dissolution.Corresponding to the SEM observation in Fig.3,both Samples SHT470 and SHT475 only have Fe-rich phase.

下载原图

Table 3 EDX analysis of constituent phases in Fig.3 (at%)

下载原图

Table 4 Phase existence in as-extruded samples after solution treatment at different temperatures

Y:existence,N:inexistence

Fig.4 Conductivity of as-extruded alloy at different conditions

In order to quantitatively analyze phase dissolution,the content of the second-phase particles treated at different conditions was statistically measured,as shown in Fig.5.The results show that solution treatment has a significant effect on phase dissolution.After holding for 2 h at450°C,the content of constituent particles in the alloy drops rapidly from 3.19 vol%to 1.87 vol%.The content of residual phases decreases with the solution temperature increasing for SHT samples.The content of residual phases in Sample SHT470 is 0.81 vol%,basically stabilizing at this value with higher increases in temperature of Sample SHT475.Correspondingly,only Fe-rich phase is observed in both samples,which is quite stable during solution treatment.Needless to say,the content of Fe-rich phase after sufficient solution treatment is 0.81 vol%and the decline of content of second phases due to dissolution of Mg(Zn,Cu,Al)2 phase and soluble elements in Fe-rich phase is 2.38 vol%.

Fig.5 Content of second-phase particles of as-extruded alloy after solution treatment at different temperatures

3.3 Effect of solution temperature on phase transformation

As mentioned before,the S(Al₂CuMg) phase transforms from Mg(Zn,Cu,Al)2 phase during solution treatment.In order to simplify the analysis,a hypothesis that diffusion coefficient is an exponential function which depends on the temperature is introduced.Hence,calculation equations of solid diffusion coefficient of Zn,Mg and Cu elements are deduced [ 14, 15] and detail information is shown in Table 5.The calculated results show that the diffusion coefficient of Zn element is almost five times bigger than that of Cu element.At low temperature,the Zn element of Mg(Zn,Cu,Al)2 phase,approached to the interface between Mg(Zn,Cu,Al)2 phase and the matrix,is dissolved into the matrix with a relatively higher diffusion rate compared with Cu element under the same surroundings.As solution treatment continues,reduction of Zn content and accumulation of Cu content make the constituent of this area in accordance with S(Al₂CuMg) phase.As a result,S(Al₂CuMg) phase appears.Apparently,the nucleation and growth of S(Al₂CuMg) phase take place in the interface frontier of Mg(Zn,Cu,Al)2 phase attached to the matrix,which is in accordance with the lamellar structure in Fig.3d.In the present work,the S(Al₂CuMg) phase is found in SHT samples treated at 450,460 and 465°C.

下载原图

Table 5 Solid diffusion coefficient (D) of Cu,Mg and Zn elements during solution treatment (m²·s^-1)

However,with the solution temperature increasing,the diffusion rate gap between Zn and Cu is narrowed.That means that the diffusion coefficient of Zn element has no significant advantage to Cu element.So it becomes difficult to match the element proportion to form S(Al₂CuMg)phase.In other words,the Mg(Zn,Cu,Al)2 phase is directly dissolved into the matrix during solution treatment.In present work,no S(Al₂CuMg) phase is found in SHT samples treated at 470 and 475°C.

So it can be concluded that the formation of S(Al₂CuMg) phase is mainly controlled by the significant diffusion rate gap between Zn and Cu during solution treatment.

4 Conclusion

Solution temperature is the main factor influencing phase dissolution.The content of residual phases decreases with the increase of the solution temperature for the SHT samples.The S(Al₂CuMg) phase transforms from Mg(Zn,Cu,Al)2 phase after solution-treated at 450,460 and 465°C,while the Mg(Zn,Cu,Al)2 phase is directly dissolved into the matrix at 470 and 475°C.The formation of S(Al₂CuMg) phase is mainly controlled by the significant diffusion rate gap between Zn and Cu during solution treatment.

Acknowledgments This study was financially supported by the National Program on Key Basic Research Project of China (No.2012CB619504) and the National Natural Science Foundation of China (No.51274046).