干燥温度对纳米β-氢氧化镍团聚程度和循环伏安性能的影响

来源期刊:中国有色金属学报2003年第5期

论文作者:赵力 张翠芬 周德瑞

文章页码:1125 - 1129

关键词:纳米材料;团聚; Ni(OH)2; 粉末微电极; 干燥温度

Key words:nano-material; agglomeration; Ni(OH)2; powder microelectrode; drying temperature

摘    要:采用沉淀转化法制备出纳米级Ni(OH)2 , 研究了干燥温度对材料团聚程度和电化学循环伏安性能的影响。 XRD 和TEM 测试结果表明: 所制备的材料为纳米级β-Ni(OH)2 , 晶粒尺寸在10~100nm之间。 干燥温度对纳米级Ni(OH)2的团聚程度有较大影响, 并可以在一定程度上控制材料的密度。 循环伏安测试表明: 适当团聚的纳米级Ni(OH)2 比微米级的具有更优越的电化学循环伏安性能, 其质子扩散系数也较大。

Abstract: Nano-scale Ni(OH)2 was prepared by precipitate transformation method. The effects of drying temperature on the agglomeration and electrochemical cyclic voltammetry of nano-scale Ni(OH)2 were investigated. The measurement results of XRD and TEM indicate that the nano-scale Ni(OH)2 prepared is β-phase and the grain size is in the rang of 10~100nm. Drying temperature has a great influence on the agglomeration degree of nano-scale Ni(OH)2 and thus can also control the density of nano-scale Ni(OH)2 within a certain extent. Cyclic voltammetry(CV) experiments show that the nano-scale Ni(OH)2 with suitable agglomeration degree has better electrochemical CV parameters and proton diffusion coefficient than micron-scale Ni(OH)2.

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 主办 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(湘)字第028号   湘ICP备09001153号