Preparation of hierarchical layer-stacking Mn-Ce composite oxide for catalytic total oxidation of VOCs
来源期刊:Journal of Rare Earths2015年第1期
论文作者:唐文翔 武晓峰 刘刚 李双德 李东艳 李文辉 陈运法
文章页码:62 - 69
摘 要:Hierarchical layer-stacking Mn-Ce composite oxide with mesoporous structure was firstly prepared by a simple precipitation/decomposition procedure with oxalate precursor and the complete catalytic oxidation of VOCs(benzene, toluene and ethyl acetate) were examined. The Mn-Ce oxalate precursor was obtained from metal salt and oxalic acid without any additives. The resulting materials were characterized by X-ray diffraction(XRD), Brunauer-Emmett-Teller(BET), scanning electron microscopy(SEM), energy dispersive X-ray spectroscopy(EDX), hydrogen temperature programmed reduction(H2-TPR) and X-ray photoelectron spectroscopy(XPS). Compared with Mn-Ce composite oxide synthesized through a traditional method(Na2CO3 route), the hierarchical layer-stacking Mn-Ce composite oxide exhibited higher catalytic activity in the complete oxidation of volatile organic compounds(VOCs). By means of testing, the data revealed that the hierarchical layer-stacking Mn-Ce composite oxide possessed superior physiochemical properties such as good low-temperature reducibility, high manganese oxidation state and rich adsorbed surface oxygen species which resulted in the enhancement of catalytic abilities.
唐文翔1,2,武晓峰1,刘刚1,2,李双德1,李东艳1,李文辉1,2,陈运法1
1. State Key Laboratory of Multi-Phase Complex Systems, Institute of Process Engineering, Chinese Academy of Sciences2. University of Chinese Academy of Sciences
摘 要:Hierarchical layer-stacking Mn-Ce composite oxide with mesoporous structure was firstly prepared by a simple precipitation/decomposition procedure with oxalate precursor and the complete catalytic oxidation of VOCs(benzene, toluene and ethyl acetate) were examined. The Mn-Ce oxalate precursor was obtained from metal salt and oxalic acid without any additives. The resulting materials were characterized by X-ray diffraction(XRD), Brunauer-Emmett-Teller(BET), scanning electron microscopy(SEM), energy dispersive X-ray spectroscopy(EDX), hydrogen temperature programmed reduction(H2-TPR) and X-ray photoelectron spectroscopy(XPS). Compared with Mn-Ce composite oxide synthesized through a traditional method(Na2CO3 route), the hierarchical layer-stacking Mn-Ce composite oxide exhibited higher catalytic activity in the complete oxidation of volatile organic compounds(VOCs). By means of testing, the data revealed that the hierarchical layer-stacking Mn-Ce composite oxide possessed superior physiochemical properties such as good low-temperature reducibility, high manganese oxidation state and rich adsorbed surface oxygen species which resulted in the enhancement of catalytic abilities.
关键词: