Investigation on pumping oxygen characteristics of (Bi2O3)0.73(Y2O3)0.27 solid electrolyte
来源期刊：JOURNAL OF RARE EARTHS2008年第3期
论文作者：LI Ying WANG Changzhen
Key words：(Bi2O3)0.73(Y2O3)0.27 solid electrolyte; oxygen sensor; oxygen pump; rare earths;
Abstract: (Bi2O3)0.73(Y2O3)0.27 fine powders prepared by wet chemical precipitation method were cold isostatically pressed to form solid electrolyte tubes, and sintered at 900 ℃ for 10 h in the air. Their pumping oxygen characteristics in non-dehydrated Ar gas were investigated, where a ZrO2 (Y2O3 stabilized) oxygen sensor was used to measure the oxygen partial pressure Po2. The results showed that the Po2 value reached magnitudes of 1×10-20-1×10-10 Pa at the applied pumping oxygen voltage of 0.5 V, 1×10-37-1×10-27 Pa at 1.0 V and 1×10-53-1×10-47 Pa at 2.0 V within the temperature range from 550 to 650 ℃. Moreover, no cracks were found in the tested solid electrolyte tubes. Thus, the Bi2O3-Y2O3 system might be used in solid electrolyte oxygen pump for purifying gases.
LI Ying1，WANG Changzhen1
(1.School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China)
Abstract:(Bi2O3)0.73(Y2O3)0.27 fine powders prepared by wet chemical precipitation method were cold isostatically pressed to form solid electrolyte tubes, and sintered at 900 ℃ for 10 h in the air. Their pumping oxygen characteristics in non-dehydrated Ar gas were investigated, where a ZrO2 (Y2O3 stabilized) oxygen sensor was used to measure the oxygen partial pressure Po2. The results showed that the Po2 value reached magnitudes of 1×10-20-1×10-10 Pa at the applied pumping oxygen voltage of 0.5 V, 1×10-37-1×10-27 Pa at 1.0 V and 1×10-53-1×10-47 Pa at 2.0 V within the temperature range from 550 to 650 ℃. Moreover, no cracks were found in the tested solid electrolyte tubes. Thus, the Bi2O3-Y2O3 system might be used in solid electrolyte oxygen pump for purifying gases.
Key words:(Bi2O3)0.73(Y2O3)0.27 solid electrolyte; oxygen sensor; oxygen pump; rare earths;