Microstructure and Corrosion Resistance of Dissimilar Weld-Joints between Duplex Stainless Steel 2205 and Austenitic Stainless Steel 316L
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2016年第3期
论文作者：Aboulfazl Moteshakker Iman Danaee
文章页码：282 - 290
摘 要：The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316 L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316 L and AWS ER 309 L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weldjoints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCl solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309 L was suitable for welding duplex stainless steel（SAF 2205） to austenitic stainless steel（AISI 316L） by gas tungsten arc welding（GTAW）process.
Aboulfazl Moteshakker，Iman Danaee
Abadan Faculty of Petroleum Engineering, Petroleum University of Technology
摘 要：The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316 L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316 L and AWS ER 309 L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weldjoints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCl solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309 L was suitable for welding duplex stainless steel（SAF 2205） to austenitic stainless steel（AISI 316L） by gas tungsten arc welding（GTAW）process.
关键词：