Effect of Pyrrole and N-Methylpyrrole Coatings on Corrosion Resistance of Mild Steel
来源期刊:材料热处理学报2004年第5期
论文作者:Ali Ghasemi S.Mailakpour Ali Ashrafi M.A.Golozar
关键词:Conductive polymer; electropolymerization; pyrrole; N-methylpyrrole; corrosion;
摘 要:Electrochemical polymerizations of various ratios of pyrrole and methylpyrrole monomers were performed in aqueous toluene-4-sulfinic acid sodium salt (T4SNa) electrolyte, using galvanostatic method. pH of electrolyte was adjusted by p-toluene sulfonic acid (PTSA). In order to prevent corrosion of mild steel substrates during coating deposition,specimens were pretreated in 0.5M oxalic acid solution, employing galvanostatic method. This would passivate the steel substrate and facilitate the coating process as well. Corrosion resistance of coated substrates was investigated in 1M NaCl solution using Tafel polarization technique. In addition, using scanning electron microscopy (SEM), morphological characterization of coatings produced, was investigated. Regarding the corrosion characteristics, results obtained revealed that the ratio of 1 to 1 (Pyrrole/Methylpyrrole) could play an important role.
Ali Ghasemi1,S.Mailakpour2,Ali Ashrafi1,M.A.Golozar1
(1.Department of Materials Engineering, Isfahan University of Technology, Isfahan, 84154, Iran;
2.Organic Polymer Chemistry Research Laboratory, College of Chemistry, Isfahan University of Technology, Isfahan, 84156, Iran)
摘要:Electrochemical polymerizations of various ratios of pyrrole and methylpyrrole monomers were performed in aqueous toluene-4-sulfinic acid sodium salt (T4SNa) electrolyte, using galvanostatic method. pH of electrolyte was adjusted by p-toluene sulfonic acid (PTSA). In order to prevent corrosion of mild steel substrates during coating deposition,specimens were pretreated in 0.5M oxalic acid solution, employing galvanostatic method. This would passivate the steel substrate and facilitate the coating process as well. Corrosion resistance of coated substrates was investigated in 1M NaCl solution using Tafel polarization technique. In addition, using scanning electron microscopy (SEM), morphological characterization of coatings produced, was investigated. Regarding the corrosion characteristics, results obtained revealed that the ratio of 1 to 1 (Pyrrole/Methylpyrrole) could play an important role.