Study on Surface and Bulk Properties of Ce-5 % Lanthanum Alloy

来源期刊:JOURNAL OF RARE EARTHS2004年增刊第1期

论文作者:Zhao Zhengping Zhang Yanzhi Fu Xiaoguo Wang Xiaolin Luo Lizhu LIU Chunrong

Key words:Ce-5% lanthanum alloy; XRD; XPS; rare earths;

Abstract: The surface and bulk properties of Ce-5% La were studied with X-ray photoelectron spectroscopy (XPS)and X-ray diffraction (XRD), respectively.The XRD analysis shows that cerium in bulk is in γ-phase, and its lattice parameter is 0.516 nm.And we also find Ce2O3 in the bulk from the XRD figure but no existence of metal lanthanum because of its small quantity.The XPS analysis shows that there are always oxides existing in the surface.The O1s peak always exists at the binding energy of 530.3 eV, which may be attributed to Ce2O3 and La2O3, but no evidence was found for the existence of CeO2.It is concluded that there is a thick layer of Ce2O3 on the sample surface.And the Ce3d peak show multi-split in the figure, in which there are two peaks in each region, 3d5/2 and 3d3/2, and the binding energy of these peaks are 882.86, 887.70 eV for 3d5/2, and 901.44, 905.93 eV for 3d3/2.The special phenomena can be attributed to the changes of 4f electronic configuration, and the cerium in the sample exhibits properties similar to Ce2O3.But the influence of the addition of lanthanum to cerium is not visible, and further investigations are expected.

详情信息展示

Study on Surface and Bulk Properties of Ce-5 % Lanthanum Alloy

Zhao Zhengping1,Zhang Yanzhi1,Fu Xiaoguo1,Wang Xiaolin1,Luo Lizhu1,LIU Chunrong1

(1.China Academy of Engineering Physics, Mianyang 621900, China)

Abstract:The surface and bulk properties of Ce-5% La were studied with X-ray photoelectron spectroscopy (XPS)and X-ray diffraction (XRD), respectively.The XRD analysis shows that cerium in bulk is in γ-phase, and its lattice parameter is 0.516 nm.And we also find Ce2O3 in the bulk from the XRD figure but no existence of metal lanthanum because of its small quantity.The XPS analysis shows that there are always oxides existing in the surface.The O1s peak always exists at the binding energy of 530.3 eV, which may be attributed to Ce2O3 and La2O3, but no evidence was found for the existence of CeO2.It is concluded that there is a thick layer of Ce2O3 on the sample surface.And the Ce3d peak show multi-split in the figure, in which there are two peaks in each region, 3d5/2 and 3d3/2, and the binding energy of these peaks are 882.86, 887.70 eV for 3d5/2, and 901.44, 905.93 eV for 3d3/2.The special phenomena can be attributed to the changes of 4f electronic configuration, and the cerium in the sample exhibits properties similar to Ce2O3.But the influence of the addition of lanthanum to cerium is not visible, and further investigations are expected.

Key words:Ce-5% lanthanum alloy; XRD; XPS; rare earths;

【全文内容正在添加中】

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号