Calculation of Thermodynamic Parameters of Mg-Al-Y Alloy
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2014年第2期
论文作者：黄文先 闫洪
文章页码：374 - 378
摘 要：By means of Miedema formation enthalpy model with Toop model, the excess free-energy, enthalpies of formation, excess entropies and activity values of all components of Mg-Al-Y ternary alloy were calculated with computer programming. The experimental results show that enthalpies of formation, excess freeenergy and excess entropies of the ternary alloy are negative in the whole content range, the minimum values at 1 123 K are all obtained at x Al=55%, x Y=45%, x Mg=0%, which are-37.969, –30.961 kJ/mol and-6.24 J/（mol·k） respectively. Activity curves show that the activity values of Al and Y in Mg-Al-Y ternary alloy rapidly decrease with the decrease of molar fraction, the values of which are very small when the molar fraction decreases to 0.4. It means that there is a strong interaction between Al and Y and stable compounds can be form in the Mg-Al-Y ternary alloy system.
黄文先1,2,3，闫洪1,3
1. Department of Materials Processing Engineering, School of Mechanical and Electrical Engineering,Nanchang University2. Department of Civil Engineering, School of Architectural Engineering, Jinggangshan University
摘 要：By means of Miedema formation enthalpy model with Toop model, the excess free-energy, enthalpies of formation, excess entropies and activity values of all components of Mg-Al-Y ternary alloy were calculated with computer programming. The experimental results show that enthalpies of formation, excess freeenergy and excess entropies of the ternary alloy are negative in the whole content range, the minimum values at 1 123 K are all obtained at x Al=55%, x Y=45%, x Mg=0%, which are-37.969, –30.961 kJ/mol and-6.24 J/（mol·k） respectively. Activity curves show that the activity values of Al and Y in Mg-Al-Y ternary alloy rapidly decrease with the decrease of molar fraction, the values of which are very small when the molar fraction decreases to 0.4. It means that there is a strong interaction between Al and Y and stable compounds can be form in the Mg-Al-Y ternary alloy system.
关键词：