CRYSTALLIZATION BEHAVIOR OF AMORPHOUS Fe86.38-1.06xW0.62+0.06xSi3B10+x ALLOYS
来源期刊:中国有色金属学报(英文版)1998年第1期
论文作者:Hu Wangyu Zhao Lihua Yang Qiaoqin Wang Lingling Zhang Bangwei
文章页码:64 - 68
Key words:thermal stability; Fe-W-Si-B alloy; glass-forming ability; microhardness
Abstract: Fe86.38-1.06xW0.62+0.06xSi3B10+x(x=0~22%, mole fraction) alloys were prepared by rapid quenching. It was found that the glass-forming range is 15%~28%B(mole fraction). The experimental results for crystallization temperatures, crystallization phases, heats of crystallization, activation energies and microhardness were presented. The crystallization temperature increases with the increase of microhardness and decreases with the increase of electron concentration. The thermal stability increases first with increasing boron content and decreases later with further increasing boron content, and the most stable case occurs at 23%B(mole fraction).