Mo-Si系机械合金化非晶转变

来源期刊:中国有色金属学报1998年第1期

论文作者:刘绍军 曲选辉 刘志坚 黄伯云

文章页码:66 - 68

关键词:机械合金化 非晶 金属间化合物

Key words:echanical alloying , amorphization , intermetallic , compound

摘    要:利用透射电镜和X射线衍射技术研究了Mo-36.5 %Si、Mo-45%Si和Mo-66.7%Si混合粉在机械合金化过程中的相结构变化。 经长时间 球磨后,这三种粉都可以转变为非晶;不同成分混合粉的中间产物并不相同,中间产物的系非晶转变的机制不同。Mo-36.5%Si的非晶化过程是首先形成亚稳相的过饱和固溶体,然后形成了非晶,此时,Mo和Si原子的尺寸因素是非晶转变的决定因素。Mo-45%Si 和Mo-66.7%Si 混和粉则是首先形成了金属间化合物,然后形成了非晶相,此时,缺陷为非晶转变的决定因素。

Abstract: The amorphization of elemental Mo and Si powder upon mechanical alloying(MA) was studied by X-ray diffraction and TEM. After long time grinding, Mo-36.5%Si, Mo-45%Si and Mo-66.7%Si mixture powders could be amorphized, but different powders had different middle products. The difference made the mechanism of amorphization different. First the amorphization procession of Mo-36.5%Si formed super-saturated solid solution, then formed amorphous state. That of Mo-45%Si and Mo-66.7% Si first formed intermetallic compound, then formed amorphous state. Key words:echanical alloying amorphization intermetallic compound



详情信息展示

 

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 主办 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(湘)字第028号   湘ICP备09001153号