包覆结构CeO2/SiO2复合磨料的合成及其应用

来源期刊:中国有色金属学报2010年第1期

论文作者:陈杨 隆仁伟 陈志刚

文章页码:163 - 169

关键词:CeO2/SiO2复合磨料;包覆;化学机械抛光,CeO2-coated SiO2 composite abrasives; coating; chemical mechanical polishing

Key words:CeO2-coated SiO2 composite abrasives; coating; chemical mechanical polishing

摘    要:以正硅酸乙酯水解所得的SiO2微球为内核,采用均匀沉淀法制备具有草莓状包覆结构的CeO2/SiO2复合粉体。利用X射线衍射仪、透射电子显微镜、X射线光电子能谱仪(XPS)、动态光散射仪和Zeta电位测定仪等手段,对所制备样品的物相结构、组成、形貌和粒径大小进行表征。将所制备的包覆结构CeO2/SiO2复合粉体用于硅晶片热氧化层的化学机械抛光,用原子力显微镜(AFM)观察抛光表面的微观形貌,测量表面粗糙度,并测量材料去除率。结果表明:所制备的CeO2/SiO2复合颗粒呈规则球形,平均粒径为150~200 nm,CeO2纳米颗粒在SiO2内核表面包覆均匀。CeO2颗粒的包覆显著地改变复合颗粒表面的电动力学行为,CeO2/SiO2复合颗粒的等电点为6.2,且明显地偏向纯CeO2;CeO2外壳与SiO2内核之间形成Si—O—Ce键,两者产生化学键结合;抛光后的硅热氧化层表面在2 μm×2 μm范围内粗糙度为0.281 nm,材料去除率达到454. 6 nm/min。

Abstract: The SiO2 nanoparticles prepared by the hydrolyzing tetraethylorthosilicate were directly coated with CeO2 by chemical precipitation technique. The as-prepared samples were analyzed with X-ray diffractometry(XRD), transmission electron microscope, X-ray photoelectron spectrometer, dynamic light scatter and Zeta potential analyzer. The thermal oxide film covered silicon wafer was polished by CeO2-coated SiO2 composite abrasives, and the polishing behavior of the novel composite abrasives was characterized by atomic force microscope (AFM). The results indicate that the monodisperse, spherical CeO2-coated SiO2 particles have a particle size of 150-200 nm and are uniformly coated by the CeO2 nanoparticles. The isoelectric point of CeO2-coated SiO2 nanoparticles is about 6.2, which displays a significant shift toward pure CeO2. The shell CeO2 is chemically bounded with SiO2 core, and the Si—O—Ce bond forms between them. The surface roughness within 2 μm×2 μm area of thermal oxide film polished by CeO2-coated SiO2 composite abrasives is 0.281 nm, and the material removal rate reaches 454.6 nm/min.

基金信息:江苏省工业支撑计划资助项目
常州市工业科技攻关资助项目

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号