Effect of Fly Ash on TSA Resistance of Cement-based Material
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第3期
论文作者：张风臣
文章页码：561 - 566
摘 要：Thaumasite form of sulfate attack（TSA）is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy （FT-IR）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive spectrum（EDS） as well as Raman spectra of erosion substances,effect of fly ash on TSA resistance of Portland cement-based material were investigated.Immersed in magnesium sulfate solution with 33 800 ppm mass concentration of SO 4 2-at 5±2℃for 15 weeks,ratio of compressive strength loss decreased as binder replacement ratio of fly ash increased.Furthermore,when binder replacement of fly ash was 60%,compressive strength increased.When thaumasite came into being in samples with 0,15%binder replacement ratio of fly ash,ettringite and gypsum appeared in those with 30%,45%,60%binder replacement ratio of fly ash.Results mentioned above showed that fly ash can restrain formation of thaumasite and improve TSA resistance of Portland cement-based material sufficiently.
张风臣
College of Mechanics and Materials,Hohai University
摘 要：Thaumasite form of sulfate attack（TSA）is a major concern in evaluating durability of concrete structures subjected to sulfate and carbonate ions.By means of Fourier transform infrared spectroscopy （FT-IR）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,and energy dispersive spectrum（EDS） as well as Raman spectra of erosion substances,effect of fly ash on TSA resistance of Portland cement-based material were investigated.Immersed in magnesium sulfate solution with 33 800 ppm mass concentration of SO 4 2-at 5±2℃for 15 weeks,ratio of compressive strength loss decreased as binder replacement ratio of fly ash increased.Furthermore,when binder replacement of fly ash was 60%,compressive strength increased.When thaumasite came into being in samples with 0,15%binder replacement ratio of fly ash,ettringite and gypsum appeared in those with 30%,45%,60%binder replacement ratio of fly ash.Results mentioned above showed that fly ash can restrain formation of thaumasite and improve TSA resistance of Portland cement-based material sufficiently.
关键词：