共搜索到7228条信息，每页显示10条信息，共723页。用时：0小时0分0秒453毫秒
THE SOLUBILITY OF FERROALLOYED NEODYMIUM IN MOLTEN SALT CONTAINING NEODYMIUM TRICHLORIDEChen Shiguan Lu Qingtao Yu Ronglin Li Xiaohua(Department of Metallurgical Engineering,Shanghai University of Technology,Shanghai 200072,P.R.China)摘 要:<正> The solubility of ferroalloyed neodymium in molten salt containing neodymium trichloride and the de......
Preparation of CaO-Al2O3-SiO2 system glass from molten blast furnace slagYing Xu1,2,Yong-zang Zhang2,Lin-yan Hou1,Xiang Lu11. College of Material Science and Engineering, Hebei United University2. Xingtai Iron and Steel Co. Ltd.摘 要:To use the potential heat of molten blast furnace slag completely,a CaO-Al2O3-SiO2system glass(MSG)was prepared from......
reduction of solid titania to titanium metal in high temperature molten chloride salts. The process has been applied to the preparation of refractory metals [11-14], ceramics [15,16], semi-metals... to titanium in molten calcium chloride [J]. Nature, 2000, 407: 361-364. [11] GIBILARO M, CASSAYRE L, LEMOINE O, MASSOT L, DUGNE O, MALMBECK R, CHAMELOT P. Direct electrochemical reduction of solid uranium......
external pressure.However,a rather well wettability of molten Mg with ceramic reinforcement is needed for this process.In order to improve the wettability of the metal melt with ceramic preform during... been successfully fabricated where Ti powder immiscible with magnesium melt was introduced into B4 C preform as infiltration inducer.The infiltration ability of molten Mg to the ceramic preform......
Electrodeposition of aluminum on aluminum surface from molten saltWenmao HUANG, Xiangyu XIA, Bin LIU, Yu LIU, Haowei WANG and Naiheng MA State Key Laboratory of Metal Matrix Composites, Shanghai Jiao... in AlCl 3 -NaCl-KCl molten salt with a mass ratio of 8:1:1 were investigated by SEM and EDS. The binding force was measured by splat-cooling method and bending method. The results indicate......
......
Electrochemical behavior of zirconium in molten NaCl-KCl-K2ZrF6 systemWU Yanke,XU Zhigao,CHEN Song,WANG Lijun and LI Guoxun Division of Mineral Resources,Metallurgy and Materials,General Research Institute for Nonferrous Metals,Beijing 100088,China摘 要:The electrochemical reduction of Zr4+(complex) ions in NaCl-KCl-K2ZrF6 molten salt on Pt electrode......
Elimination of phosphorus vaporizing from molten silicon at finite reduced pressure ZHENG Song-sheng1, 2, Jafar SAFARIAN 2, Seongho SEOK3, Sungwook KIM3, Tangstad MERETE2, LUO Xue-tao1 1... molten silicon as gas species P and P2 at a finite reduced pressure. The experimental results show that phosphorus mass fraction can be decreased from 0.046% (460ppmw) to around 0.001% (10ppmw) under......
chloride solution showed that the corrosion potential shifted to more negative values with additions of Sb, Bi and Sr, respectively. Corrosion immersion tests also revealed that the element additions have a detrimental effect on the corrosion rate of alloys, due to the increase of boundaries between the Al and eutectic Si phases. Key words: aluminium die cast alloy; melt treatment; mechanical......
Effect of melt convection on primary dendrite arm spacing in directionally solidified Pb-26%Bi hypo-peritectic alloys HU Xiao-wu, LI Shuang-ming, GAO Si-feng, LIU Lin, FU Heng-zhi State Key... phase in directionally solidified Pb-26%Bi (mass fraction) hypo-peritectic alloys was measured by considering the effect of melt convection in cylindrical samples with different diameters......