共搜索到18689条信息，每页显示10条信息，共1869页。用时：0小时0分0秒250毫秒
新型高强高导接触导线用Cu-Cr-Zr系合金研究进展周倩1,李雷1,李强1,谢水生2,黄国杰21. 河南理工大学材料科学与工程学院2. 北京有色金属研究总院有色金属制备加工国家重点实验室摘 要:总结了国内外电气化高速铁路接触网用接触导线的研究和使用现状,讨论了高强高导Cu-Cr-Zr系合金应用于新一代国产化接触线的必要性和可行性.分析了Cu-Cr系合金中所添加的Zr,Mg,Sn,Ti,Si及RE等不同元素对合金性能的影响,概述了当前对于Cu-Cr-Zr系合金导电率,强度,耐磨性和抗软化性等合金性能的研究现状,总结了高强高导Cu-Cr-Zr系合金在制备工艺方面的研究情况,提出几个亟待解决的问题及对进一步的研究做出展望.关键词:接触导线;Cu-Cr-Zr系合金;高强高导;......
and prevention of Cu-Cr-Zr alloy ingots[J]. Foundry Technology, 2006, 27(11): 1205-1209. [5] WEI Jun-wei, WANG Xin-zheng. Analysis and preventive measures of common defects of copper alloy extruded products[J... 2007; accepted 10 September 2007 Abstract: To promote the solution of chromium in copper and the purity of copper-chromium (Cu-Cr) alloy, vacuum continuous casting (VCC) process was employed......
La,Fe(或Co)/Ti对Cu-Cr-Zr合金时效特性的影响 铃木洋夫1,余学涛2,黄福祥1,郭淑梅2,宁洪龙1,王涛2,马莒生1,耿志挺1,李红2,李鑫成2 (1.清华大学,北京,100084;2.洛阳铜加工集团,河南,洛阳,471039) 摘要:研制了新型集成电路引线框架Cu-Cr-Zr系列合金,通过电导率,硬度,抗拉强度测试以及透射电镜观察,考察了微量合金元素La,Fe/Ti,Co/Ti元素以及时效工艺对合金性能的影响.结果表明:稀土元素La可以改善A合金(Cu-Cr-Zr-Zn)的硬度及导电率;加入Fe/Ti,Co/Ti元素,大大提高了合金的强度和硬度,并使其时效的强度及硬度峰值延后.在970℃固溶处理,70%冷变形及不同温度时效2 h后,A合金(Cu-Cr-Zr-Zn)及B合金(Cu-Cr-Zr-Zn-La)在450℃时达到硬度和强度峰值,分别为HV 1 770 MPa......
Microstructure and Performances of Nanocrystalline Zinc-nickel Alloy Coatings LI Guang-yu1,NIU Li-yuan1,JIANG Zhong-hao1,LIAN Jian-she1 (1.The Key Lab of Automobile Materials, Ministry of Education, China, College of Materials Science and Engineering, Jilin University, Nanling Campus, Changchun, 130025, China) 摘要:Nanocrystalline zinc-nickel alloy coatings were deposited from an alkaline......
Alloy 20不锈钢薄板等离子弧焊接工艺研究赵斌,王宾宾,王小华中国船舶重工集团公司第七二五研究所摘 要:对Alloy 20不锈钢薄板进行了等离子弧焊接工艺试验研究.结果表明,采用等离子弧焊接方法,ERCr Ni Mo-3焊材及合理的焊接工艺参数,等离子弧焊接工艺可用于Alloy 20不锈钢薄板的焊接,焊接接头各项性能均能满足要求.关键词:Alloy 20;不锈钢薄板;等离子弧焊接;......
on the properties and microstructure of Cu-Cr-Zr alloy and Cu-Cr-Zr-Ag alloy were investigated. Ag addition improves the mechanical properties of the alloy through solid solution strengthening and brings a little effect on the electrical conductivity of the alloy. A new Cu-Cr-Zr-Ag alloy was developed, which has an excellent combination of the tensile strength, elongation, and electrical conductivity......
时效处理对快速凝固Cu-Cr-Zr合金组织和性能的影响刘平,黄金亮,顾海澄,曹兴国,康布熙摘 要:采用单辊快速凝固方法制备出高强度高导电的Cu－Cr－Zr合金,对时效过程中电阻率和显微硬度的变化进行了研究,用扫描电镜和透射电镜对析出过程中晶粒与析出相的形态与大小及位错的组态进行分析．结果表明:时效初期电阻率的下降是溶质原子借高浓度的空位迅速偏聚和析出所致.在500℃温度下,时效30min,合金的导电率可达82％IACS,显微硬度为Hv202.细小弥散分布的析出相是导致高硬度的主要原因.关键词:快速凝固;CU－Cr－Zr合金;时效处理;......
)Abstract:Stainless die with micro-groove and micro-hole have been designed and manufactured, which has been used to study superplastic microforming of 2091Al-Li alloy by means of superplastic forming... micro-rib specimen, behavior of material could be understood well.Key words:superplasticity; microforming; extrusion; 2091Al-Li alloy......
连续挤压对Cu-Cr-Zr合金组织与性能的影响吕昭弟1,宋练鹏1,2,王凯1,张龙11. 中南大学材料科学与工程学院2. 中南大学有色金属材料科学与工程教育部重点实验室摘 要:对Cu-0.71Cr-0.04Zr合金热挤压棒材进行连续挤压,得到相同直径的连续挤压棒材,采用扫描电镜(SEM),透射电镜(TEM)以...0.51μm之间,夹杂少量平均尺寸约200nm的等轴再结晶晶粒,同时伴有细小的析出相析出.关键词:连续挤压;Cu-Cr-Zr合金;晶粒取向;形变;析出相;......
非真空熔铸Cu-Cr-Zr合金的热变形行为及加工图丁宗业1,贾淑果1,2,李湘海3,郭望望1,王俊峰1,刘平11. 河南科技大学材料科学与工程学院2. 河南省有色金属材料科学与加工技术重点实验室3. 中铝洛阳铜业有限公司摘 要:利用Gleeble-1500热模拟实验机对非真空熔铸Cu-0.94Cr-0.34Zr合金进行高温热压缩变形,研究在变形温度为500~800℃,应变速率为0.01~1 s-1工作条件下该合金的流变应力行为,建立合金热变形流变应力本构方程及加工图.结果表明:流变应力随变形温度的升高而降低,随应变速率的降低而减小;可用包含Zener-Hollomon参数的Arrhenius双曲正弦关系式描述Cu-0.94Cr-0.34Zr合金的热变形行为,建立本构方程,算出其激活能为418.35......