in a vacuum oven for 12 h at 80 °C, which was further cut into wafers with a diameter of 12.0 mm. The final mass of electroactive materials was approximately 1.2 mg/cm. The galvanostatic charge......
sintered in a vacuum of 1×10-5 Pa, 1400 °C for 8 h. The sintered samples were cut into 10 mm-high columns, and then repeatedly hot rolled and heated in air at 750 °C, with a total reduction......
alloy under four conditions: (1) the sample was sealed in vacuum glass tube and aged at 100, 20 and 0 °C (marked as Conditions A, B and C, respectively); (2) the sample was first sealed with paraffin......
Press, 2010. (in Chinese) [28] LIU Kang, YANG Jia-kuang, LIANG Sha, HOU Hui-jie, CHEN Ye, WANG Jun-xiong, LIU Bing-chuan, XIAO Ke-ke, HU Jing-ping, WANG Jin. An emission-free vacuum chlorinating......
decoupling control of double-level air flow field dynamic vacuum system based on neural network and prediction principle [J]. Engineering Applications of Artificial Intelligence, 2013, 26(4......
was prepared by using vacuum induction melting (VIM) and electroslag remelting (ESR). The diameter of VIM ingot was 280 mm. The main chemistry composition of VIM ingot was 3.7% Al, 2.8% Ti, 3.4% Nb......
on the Cu-Mg-Fe alloy hot deformation behavior [J]. Vacuum, 2018, 155: 594-603. [34] ZHANG Yi, LIU Ping, TIAN Bao-hong, LIU Yong, LI Rui-qin, XU Qian-qian. Hot deformation behavior and processing map of Cu......
be controlled in appropriate nucleation period, and the final particle number does not change in that time. The resulted composite was filtered, washed out and kept in a vacuum oven at 60 °C to obtain......
and modified malachite were washed with methanol-water (1:1, volume ratio) mixed solution several times to eliminate any residual surfactant and later dried with a vacuum. 2.5 XPS analysis An XPS......