共搜索到189条信息，每页显示10条信息，共19页。用时：0小时0分0秒322毫秒
Deformation behavior and microstructure of an Al-Zn-Mg-Cu-Zr alloy during hot deformationLiang-ming Yan,Jian Shen,Jun-peng Li,Zhou-bing Li,and Xiao-dong Yan General Research Institute for Nonferrous Metals,Beijing 100088,China摘 要:The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot......
Trans. Nonferrous Met. Soc. China 24(2014) 2475-2481 Microstructural evolution of gas atomized Al-Zn-Mg-Cu-Zr powders during semi-solid rolling process Feng-xian LI1,2, Yun-zhong LIU2, Jian-hong YI1... F Y, WANG G J, LI Z C, SUN J F. Microstructural evolution during extrusion and ECAP of a spray deposited Al-Zn-Mg-Cu-Sc-Zr alloy [J]. Journal of Materials Science, 2010, 45: 3023-3029. [16] DELPLANQUE......
微量钪对Al-9.0Zn-2.5Mg-1.2Cu-0.15Zr合金组织性能的影响 王银娜1,夏长清1,邰凯平1,戴晓元1,吴安如1 (1.中南大学,材料科学与工程学院,湖南,长沙,410083;2.长沙理工大学,汽车机械学院,湖南,长沙,410076) 摘要:采用铸锭冶金法制备了Al-9.0Zn-2.5Mg-1.2Cu-0.15Zr和Al-9.0Zn-2.5Mg-1.2Cu-0.12Sc-0.15Zr合金,采用金相显微镜,扫描电子显微镜和透射电子显微镜研究了2种合金不同处理态的显微组织,测试了不同热处理状态下合金的力学性能和电导率.结果表明:添加微量Sc可以明显细化合金的铸态晶粒,显著提高Al-Zn-Mg-Cu-Zr合金的力学性能和电导率,其作用机理主要为Al3(Sc,Zr)引起的细晶强化,亚结构强化和沉淀强化. 关键词:Sc; Al-Zn-Mg-Cu-Zr合金; 力学性能; 电......
Al-11.7Zn-2.2Mg-2.0Cu-0.12Zr铝合金不同固溶温度处理后的组织与性能变化规律进行了研究.结果表明:晶内的固溶度随温度升高逐渐增加,在474℃时基本达到稳定状态,约有99%的Zn,Mg以及75%的Cu溶入晶内,其余的合金元素富集在晶界第二相内,此时,第二相主要由含Cu的η以及T相构成;合金的最佳固溶温度为474℃,此时合金的抗拉强度(σb)为688 MPa,延伸率(δ)为8%;温度为476℃时,合金局部区域出现轻微过烧,导致延伸率迅速降低;断口分析显示,随固溶温度的提高,再结晶程度增加,晶界第二相数量减少,合金的拉伸断口由较低温度时的沿晶+穿晶混合断口转变为较高温度时的沿晶断口为主.关键词:Al-Zn-Mg-Cu-Zr合金;固溶温度;第二相粒子;再结晶;断口形貌;......
Al-Zn-Mg-Cu-Zr-0.5Er合金型材组织性能研究王少华,马志锋,张显峰,孙刚,冯朝辉,李伟,陆政北京航空材料研究院摘 要:采用金相,扫描电镜,电子背散射衍射,透射电镜分析及拉伸性能实验等测试分析手段,研究了Al-Zn-Mg-Cu-Zr-0.5%Er合金型材的组织性能.结果表明,合金型材中的元素Er主要以未溶的Al8Cu4Er相形式存在,该粒子可以钉扎位错和晶界的迁移,有效抑制合金回复再结晶和晶粒长大,保持合金的变形态组织.0.5%Er的添加使得合金型材的强度降低,主要是因为合金型材中残留了大量的Al8Cu4Er相,在变形过程中由于位错塞积形成裂纹,降低了合金的强度.但是,合金的电导率有所提高.关键词:Al-Zn-Mg-Cu-Zr合金;铒;Al8Cu4Er相;显微组织;力学性能;......
究含钪Al-Zn-Mg-Cu-Zr系铸态合金在退火过程中二次Al3(Sc,Zr)粒子的析出形貌,尺寸及分布.结果表明:含0.20%Sc的7系铝合金铸态试样在450 ℃退火2 h后,α(Al)基体内析出呈豆瓣状的二次Al3(Sc,Zr)粒子；在450 ℃退火32 h后,Al3(Sc,Zr)粒子尺寸为16~23 nm；在450 ℃退火32 h后的二次Al3(Sc,Zr)相与α(Al)基体完全共格...(Sc, Zr) secondary particles in Al-Zn-Mg-Cu-Zr alloy containing Zr during annealing were studied by transmission electron microscopy. The results show that the bean-like Al3(Sc, Zr) secondary......
文章编号:1004-0609(2013)04-0912-07 Al-Zn-Mg-Cu-Zr-Yb铝合金中弥散相的形成和作用 董朋轩,陈康华,方华婵,彭国胜 (中南大学 粉末冶金国家重点实验室,长沙 410083) 摘 要:采用金相,能谱分析,扫描电镜,透射电镜和力学性能实验,研究Al-Zn-Mg-Cu-Zr-Yb铝合金中弥散相的形成以及弥散相对铝合金显微组织,再结晶行为,拉伸性能和断裂韧性的影响.结果表明:在Al-Zn-Mg-Cu-Zr-Yb合金中形成了大量,细小,分布均匀,与基体共格的L12型Al3(Zr,Yb)弥散相；与Al-Zn-Mg-Cu-Zr中形成的Al3Zr弥散相相比,Al3(Zr,Yb)弥散相能更有效地抑制合金变形-固溶过程中的再结晶,合金屈服强度提高了6%,断裂韧性提高35%. 关键词:Al-Zn-Mg-Cu-Zr......
匝数对铸锭元素晶内固溶度和力学性能的影响规律.结果表明,相对常规DC铸造,低频电磁铸造组织细小均匀等轴,合金元素Zn,Mg和Cu在晶内的固溶度增加,铸态维氏硬度,延伸率和拉伸强度增加.频率为15~25Hz和安匝数12800~16000AT时,合金元素Zn,Mg和Cu在晶内的固溶度最高,锭坯维氏硬度,延伸率和拉伸强度最大.其φ12mm的挤压棒材热处理后的拉伸强度极限为780MPa,延伸率大于8%. 关键词:低频; 电磁铸造; 固溶度; 力学性能; Al-Zn-Mg-Cu-Zr; [全文内容正在添加中] ......
; Abstract: Al-Zn-Mg-Cu-Zr alloys containing Yb were prepared by cast metallurgy. Effect of 0.30% Yb additions... and stress corrosion cracking test. The results show that the Yb additions to high strength Al-Zn-Mg-Cu-Zr aluminum alloys can produce fine coherent dispersoids. Those dispersoids can strongly pin dislocation......
微量Zr元素对Al-Zn-Mg-Cu合金阳极化效果的影响王瑞雪,罗阳,汪磊西南铝业(集团)有限责任公司摘 要:采用铸锭冶金法制备了Al-Zn-Mg-Cu和Al-Zn-Mg-Cu-Zr两种合金,并利用岛津AGS-X-100KN电子万能材料试验机测试了不同成分试样的力学性能;利用数码显微镜,金相显微镜研究了2种合金纵截面不同厚度位置的阳极氧化效果及显微组织形貌.结果表明,添加微量的Zr可以明显抑制Al-Zn-Mg-Cu合金的再结晶程度;但由于Al3Zr粒子的弥散分布程度不均匀,导致合金整个厚度截面组织不均匀,并最终影响板材成品的阳极化效果.可通过优化均热制度工艺的方法对其进行改善.关键词:Zr元素;Al-Zn-Mg-Cu合金;显微组织;阳极氧化;......