共搜索到180180条信息，每页显示10条信息，共18018页。用时：0小时0分0秒696毫秒
) 原始铝合金粉颗粒间的界面; 2) Al2O3小颗粒与基体的界面; 3) SiC颗粒与铝合金基体的界面. 图5所示为粉末混合-半固态挤压法制得的SiCp/2024铝合金复合材料的典型界面形貌. 由于挤压过程中铝合金粉颗粒表面氧化膜破碎, 从而使铝合金粉结合成致密的复合材料基体, 并且半固态挤压过程中有液相的存在, 更有利于局部未结合好的界面愈合. 从图5 (a) 可以看到Al基体的晶界非... 88.3 8.4 图5 SiCp/2024铝合金复合材料干净界面的TEM形貌 Fig.5 TEM micrographs showing clean interface in SiCp/2024 Al alloy composites (a) -550 ℃; (b) -570 ℃ 3) 粉末混合-半固......
态抗拉强度可达到868 MPa,说明元素粉末中添加的预合金粉可以控制烧结过程,提高合金的烧结密度,同时增强合金的力学性能. 关键词:Ni-Fe-Al合金；机械合金化；粉末冶金 中图分类号:TG 113.25；TF 124 文献标识码:A Influence of prealloyed powder on properties... Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) Abstract: Ni-Fe-Al alloys were made by powder metallurgy from mixing the elementary powder Ni, Fe and Al......
;Morphology and EDS mapping distribution results of Ti-45Al-8Nb sintering at 1 200 ℃ for 1 h 3 结论 1) 高Nb含量TiAl金属间化合物元素粉末的反应中,铝液熔化包裹在Ti与Nb颗粒表面,Ti-Al反应随着温度的升高,反应程度不断升高. 2) 同一温度下的Ti-Al反应并不是单一某种反应,而是多种...合物制备过程中,铝熔化后包裹在Ti与Nb颗粒表面,Ti原子与Al原子相互扩散,Ti-Al反应随着温度的升高,反应程度不断升高.同一温度下的Ti-Al反应并不是单一反应,而是多种Ti-Al系反应共存.在1 200 ℃反应中,Ti基本反应完全,但是单相Nb依然存在.在1 000 ℃反应后,依然有单相α-Ti存在,从而有望提高固结后材料的可加工性能. 关键词:TiAl金属间化合物；粉末冶金；元素粉末反应......
. Lastly, using Formula (3), the contents of the analytes in MnZn ferrite powder were obtained. (1) ...)= 1 : 3. R is the mass ratio of MnZn ferrite to copper powder. 3 Results and discussion 3.1 Sample pretreatment conditions There are significant differences in the conductivity between sample tablets......
试样制备 实验选用的试剂均为分析纯,包括氯化钠(NaCl),氯化钙(CaCl2),氯化铅(PbCl2)和氯化亚锡(SnCl2),所用Al片为原铝,纯度大于99.7%. Al基体表面熔盐化学镀Pb的过程包括以下步骤:1) 熔盐准备:按要求称量一定量的干燥的氯化物,搅拌均匀,并在马弗炉中加热至设定的温度后,保温3 h；2) Al片预处理:Al片经过200#和400#砂纸打磨后,水洗...条件优化 2.2.1 过热度 熔盐初晶点与实际使用温度之间的差值,称为过热度.一般说来,熔盐的实际使用温度都要超过其初晶温度,一方面可以保证熔盐始终处于熔融状态,并具有良好的流动性；另一方面温度对化学反应和原子扩散速度影响较大.在Al基体表面进行化学镀Pb,就是利用新生态的Pb原子能够在新鲜的铝表面扩散,附着,以期增加两者的结合强度. 固定Al片浸入熔盐时间为3 min,在不同的......
micro- powder before and after surface modification 颗粒表面改性前后增强Al复合材料的制备采用挤压铸造专利技术[10]. 挤压铸造工艺为: 预制块预热温度580~600℃, 浇铸温度850~950℃, 压铸压力70~80MPa, 保压时间180s. 材料制备过程中渗透压的变化由压力曲线测得. 铝合金-α-Al2O3接触角测定在STMD300型表...同一温度下Al熔滴与改性的Al2O3 图3 Al-Al2O3体系的接触角随温度的变化 Fig.3 Variation of contact angles with temperature for system Al-Al2O3 determined by both as-received Al2O3 powder and coated powder 基片间的接触......
mechanical properties and wear resistance are demanded. Tables 2 and 3 show the properties of the Al matrix and SiC reinforcement, respectively. The stir casting furnace was mounted on the floor... for the unreinforced alloy and composites investigated in this study. It is observed that the addition of hard ceramic SiC particles increases the hardness of Al alloy. Fig. 3 Effect of SiC content......
=93.67?,β=118.92?,γ=70.27?. 图1 氢氧化铝晶体的计算模型 Fig.1 Calculation models of three kinds of Al(OH)3 crystals: (a) Gibbisite; (b) Bayerite; (c) Nordstradite 基于密度泛函理论(Density functional theory...小0.786 54 eV和0.858 87 eV.诺耳石最低和最高能隙则分别位于G(0,0,0)点和Q(0,1/2,1/2)点.由此可推测三水铝石的反应活性可能比拜耳石和诺耳石的稍高. 2.4 布居分析 图9所示为不同基组水平下,各研究体系中H,O和Al原子的总平均布居数及平均电荷的计算结果.可见,整体上,3种氢氧化铝晶体中的H,O和Al原子的原子净电荷绝对值均分别小于各自的表征电......
technology for creating similar and dissimilar joints from challenging materials [3]. However, uncontrollable formation of TiAl and TiAl3 intermetallics caused by direct contact of Al and Ti in solid... be used for several reasons including: (1) to avoid or reduce the possibility of formation of brittle IMCs, (2) to eliminate the harmful effects of Ti and Al oxide films, (3) supplying appropriate......
别进行低温加热,高温氧化和高温氧化后酸洗处理,即进行:原始态处理(置于箱式电阻炉中于200 ℃加热以除去结晶水和吸附物),氧化态处理(置于刚玉坩埚中于1100 ℃分别氧化6,10 h),酸洗态处理(原始态和氧化态样品在5%的氢氟酸中浸泡3 h后烘干). 在不同状态下,体积分数为13%的SiC与6066铝合金粉末球磨混料后冷等静压成锭坯,然后于410 ℃以16∶1的挤压比挤压成棒材.挤压棒材于...尖(角度越小),应力集中越严重,在基体中离颗粒一样远的地方,尖角处的应力远远高于平滑处的应力.由热错配应力造成的基体微区应力场很强,对于Al-SiC体系,增强体颗粒引起基体周围的塑性变形硬化区半径与颗粒的半径相近.在实际复合材料中,增强相并不是均匀分布,往往出现几个SiC颗粒团聚在一起的现象,这时几个带有棱角的SiC颗粒周围的张应力场相互叠加(见图3),轴向张应力互相叠加后形成张应力区,导致微裂纹......