共搜索到7709条信息，每页显示10条信息，共771页。用时：0小时0分0秒643毫秒
increasingly close to the Scheil profiles as the solidification rate decreased. The simulated microstructure and microsegregation in an Al-Cu-Mg ternary alloy were compared with those obtained experimentally. Key words: solidification; modeling; microstructure; microsegregation; Al-Cu-Mg ternary alloy 1 Introduction Solidification microstructure and microsegregation of castings are very important......
properties and microstructures of Al-Cu-Mg alloy with a high Cu content (8%, mass fraction) wasreported, with the focus on the formation and coarsening of the θ′ and Ω phases, and the effect... the inherent incompatibility between the particles and the Al matrix during deformation. Key words: Al-Cu-Mg alloy; mechanical properties; microstructures; Ag addition 1 Introduction Heat-treatment......
Al-Cu-Mg系高强铝合金的晶间腐蚀牟春西南铝业(集团)有限责任公司摘 要:简述了Al-Cu-Mg系高强铝合金晶间腐蚀的原理及其影响因素,从合金成分,加工工艺,热处理三个方面分析了控制晶间腐蚀的方法.关键词:Al-Cu-Mg合金;晶间腐蚀;成分;热处理;......
文章编号:1004-0609(2007)07-1034-07 Al-Cu-Mg合金的断裂韧性与拉伸延性模拟 宋旼,袁铁锤,张福勤,黄伯云,陈康华 (中南大学 粉末冶金国家重点实验室,长沙 410083) 摘 要:基于铝合金中的脆性结晶相在外力作用下发生断裂而形成微裂纹的过程服从Weibull分布,建立了Al-Cu-Mg合金断裂韧性与拉伸延性的细观力学模型.模型的解析表明,在外力作用下由结晶相断裂而形成的微裂纹的体积分数随着外加应力的增加而增加；在相同的外加应力作用下,结晶相含量较高时微裂纹的体积分数也较高.同时模型的计算表明,Al-Cu-Mg合金的拉伸延性及断裂韧性与结晶相的含量及尺寸有很大关系；拉伸延性与断裂韧性随着结晶相体积分数与尺寸的增加而减小；因此通过对铝基体的纯化,减少Fe与Si元素的含量或者通过强化固溶处理可以降低结晶相的体积分数与尺寸,从而提......
Flow stress behavior of high-purity Al-Cu-Mg alloy and microstructure evolutionLI Li(李立)1, LI Hui-zhong(李慧中)1, 2, 3, LIANG Xiao-peng(梁霄鹏)2, HUANG Lan(黄岚)2, HONG Tao(洪涛)4(1. School of Materials... behavior of high-purity Al-Cu-Mg alloy under hot deformation conditions was studied by Gleeble-1500, with the deformation temperature range from 300 to 500 °C and the strain rate range from 0.01 to 10 s-1......
zones, S"-, S'- and S-phases in an Al-0.9%Cu-1.4%Mg alloy [J]. Acta Mater, 2000, 48(10): 2751-2764. [17] Shih H C, Ho N J, Huang J C. Precipitation behaviors in Al-Cu-Mg and 2024 aluminum alloys [J.... Two types of S phase precipitates in Al-Cu-Mg alloys [J]. Acta Mater, 2007, 55(3): 933-941. [21] Wang S C, Starink M J. Precipitates and intermetallic phases in precipitation hardening Al-Cu-Mg-(Li......
Ag含量对Al-Cu-Mg合金组织和性能的影响宋艳芳1,潘清林1,2,曹素芳1,王迎1,李晨11. 中南大学材料科学与工程学院2. 有色金属材料科学与工程教育部重点实验室摘 要:采用维氏硬度,室温拉伸性能测试,金相显微分析技术,透射电子显微分析等手段,研究Ag含量对Al-Cu-Mg耐热铝合金组织和性能的影响.结果表明:随着Ag含量的增加,室温时Al-Cu-Mg合金的屈服强度和抗拉强度增加,塑性逐渐降低,但总体保持在较高水平;合金的硬化速率加快,峰时效提前,峰值硬度提高;不含Ag的Al-Cu-Mg合金中的强化相为θ’相,添加微量Ag后,Al-Cu-Mg合金的主要强化相为Ω相,且随着Ag含量的增加,Ω相的含量也逐渐增加,Ag能够促进Ω相的析出.关键词:Al-Cu-Mg合金;Ag含量;显微组织......
预拉伸变形对Al-Cu-Mg合金腐蚀性能的影响林茂,刘志义,陈来,王恒,柏松中南大学材料科学与工程学院摘 要:采用表面腐蚀,慢应变速率拉伸(SSRT)实验研究预拉伸变形对Al-Cu-Mg合金腐蚀性能的影响.利用扫描电镜观察分析Al-Cu-Mg合金断口形貌及结构.结果表明,预拉伸变形可显著提高合金位错密度,为H原子的扩散提供更多的通道,因此,在相同腐蚀时间下,3.5%Na Cl溶液中T8态Al-Cu-Mg合金的腐蚀速率高于T6态.此外,预拉伸变形可显著增加S相弥散度,使得S相两侧的无沉淀析出带变窄,有效降低了晶界和晶内的电位差,从而降低晶界沉淀相的溶解速度,因此,在同一热处理状态下,Al-Cu-Mg合金在饱和H2S溶液中的应力腐蚀开裂敏感性高于干燥空气中的腐蚀开裂敏感性.同一应变速率下,T8态Al-Cu......
, Sakurai T, Polmear I J. Origins of hardening in aged Al-Cu-Mg-(Ag) alloys[J]. Acta Mater, 1997, 45 (9): 3731-3744. [3] Wolverton C. Crystal structure and stability of complex precipitate phases in Al-Cu...基于人工神经网络的Cu与Mg低质量比Al-Cu-Mg合金时效强化预测模型 侯延辉1, 2,刘志义2,邓才智2,刘延斌2,马飞跃2 (1. 西南交通大学 应用力学与工程系,四川 成都,610031； 2. 中南大学 材料科学与工程学院,湖南 长沙,410083) 摘 要:通过硬度检测和透射电镜(TEM)观察,研究低Cu/Mg质量比Al-Cu-Mg合金时效强化机理,建立神经网络预......
......