共搜索到10899条信息,每页显示10条信息,共1090页。用时:0小时0分0秒312毫秒
Berberine as an Environmental-Friendly Inhibitor for Hot-Dip Coated Steels in Diluted Hydrochloric AcidHong Ju, Yulin Ju and Yan Li College of Mechanic and Electronic Engineering, China University of Petroleum, Qingdao 266555, China摘 要:The inhibition effect of an excellent environmental-friendly corrosion inhibitor-berberine on hot-dip coated steels......
Research on anti-corrosion property of rare earth inhibitor for X70 steel朱艳华1,庄稼1,于永生1,曾宪光1,21. School of Materials Science and Engineering,Southwest Petroleum University2. Material Corrosion... inhibitors(La(NO3)3+Na2MoO4(LaN-M),Ce(NO3)3+Na2MoO4(CeN-M),Pr(NO3)3+Na2MoO4(PrN-M)).The combination of weight-loss method and the electrochemical test,was used to evaluate and analyze the corrosion......
Research on anti-corrosion property of rare earth inhibitor for X70 steel朱艳华1,庄稼1,于永生1,曾宪光1,21. School of Materials Science and Engineering,Southwest Petroleum University2. Material Corrosion... inhibitors(La(NO3)3+Na2MoO4(LaN-M),Ce(NO3)3+Na2MoO4(CeN-M),Pr(NO3)3+Na2MoO4(PrN-M)).The combination of weight-loss method and the electrochemical test,was used to evaluate and analyze the corrosion......
......
of impurity in matrix.In addition,NaOH solution was chosen as inhibitor to prevent Gd from being corroded successfully.No pitting corrosion and weight loss were observed for commercial Gd even after...Corrosion Behavior of Commercial Magnetic Refrigerant Gadolinium in Water Wen Da1,ZHANG Zeyu1,Ye Rongchang1,Long Yi1,WAN Farong1 (1.School of Materials Science and Engineering, University......
Trans. Nonferrous Met. Soc. China 26(2016) 3034-3045 Control of zinc corrosion in acidic media: Green fenugreek inhibitor Shimaa M. ALI1,2, Hamedh A. Al LEHAIBI1 1. Department of Chemistry, Faculty... 2016 Abstract: Fenugreek seeds extract was examined as a green corrosion inhibitor for Zn in 2.0 mol/L H2SO4 and 2.0 mol/L HCl solutions by mass loss and electrochemical measurements. Scanning electron......
焦炭劣化抑制剂对焦炭热性能的改善研究王留成1,郑士朋1,王建设1,宋成盈1,赵建宏1(1.河南省郑州市郑州大学化学工程学院)摘 要:通过与H3BO3作对比,考察了新型焦炭劣化抑制剂A,B,ZP对焦炭热性能的影响,ZP新型焦炭劣化抑制剂改善焦炭热性能的作用比其它3种劣化抑制剂更显著.为便于工业化应用,研究了浸泡和喷洒方式对ZP作用的影响,结果表明:浸泡方式更有利于ZP作用的发挥.为进一步认识ZP作用机理,用扫描电子显微镜观察了喷洒ZP对热反应前和后焦炭形貌的影响,结果表明:喷洒ZP后焦炭表面气孔直径和深度都减小,......
Trans. Nonferrous Met. Soc. China 27(2017) 711-721 Anodising of 2024-T3 aluminium alloy in electrolyte of sulphuric-boric-phosphoric mixed acid containing cerium salt as corrosion inhibitor Mohsen... acid; cerium salt; inhibitor 1 Introduction Aluminium alloys containing copper (2000 series) exhibit high strength and are widely used in the aviation industry but generally they show low corrosion......
as an environmentally friendly corrosion inhibitor for steel was investigated in 1 mol/L HCl using potentiodynamic polarization, electrochemical impedance spectroscopy and chronoamperometry measurements. All electrochemical measurements suggest that this compound is an excellent corrosion inhibitor for mild steel and the inhibition efficiency increases with the increase in inhibitor concentration......
of the inhibitor mixture and to explain the nature of this effect. Corrosion properties of the inhibitor layer were studied using the electrochemical impedance spectroscopy (EIS), while the resistance... aluminium alloy was smaller than that formed in artificially aged alloy. The synergistic effect of the inhibitor mixture on corrosion properties of naturally aged alloy was observed throughout 96 h......