共搜索到69557条信息，每页显示10条信息，共6956页。用时：0小时0分0秒749毫秒
treatments on precipitation process, microstructural development and mechanical properties of 6061 alloy were studied by BUHA et al [7]. They focused on secondary precipitation using transmission electron...-forged Al 6061 alloy [J]. Materials Science and Engineering A, 2008, 485: 272-281. [7] BUHA J, LUMLEY R N, CROSKY A G. Microstructural development and mechanical properties of interrupted aged Al-Mg-Si......
Trans. Nonferrous Met. Soc. China 25(2015) 2866-2874 Electrical discharge machining of 6061 aluminium alloy A. PRAMANIK1, A. K. BASAK2, M. N. ISLAM1, G. LITTLEFAIR3 1. Department of Mechanical..., Australia Received 24 November 2014; accepted 18 March 2015 Abstract: The wire electrical discharge machining (EDM) of 6061 aluminium alloy in terms of material removal rate, kerf/slit width, surface......
over the melting temperature (580 to 660 °C) of 6061 Al alloy. Figure 11 shows that the removed material of MMC is very irregular in shape and has a dark texture. The size of detached debris increases... under similar experimental conditions were compared on a pin-on-disc wear machine. The pins were made of 6061 aluminum matrix alloy and 6061 aluminum matrix composite reinforced with 10% Al2O3 (volume......
T6I6时效对6061铝合金拉伸及晶间腐蚀性能的影响李海1,潘道召2,王芝秀2,郑子樵3(1.江苏省常州市江苏工业学院材料科学与工程系2.江苏工业学院 材料科学与工程学院3.中南大学 材料科学与工程学院,湖南 长沙,410083)摘 要:对T6I6时效处理的6061铝合金的拉伸性能,晶间腐蚀性能和电导率进行了测试,并采用OM和TEM对其组织进行了观察.结果表明,6061铝合金经180℃×8 h T6峰值时效后,虽然强度较高,但有严重晶间腐蚀倾向;T6I6预时效时间对拉伸性能影响不大,但中断时效温度和时间对其影响显著.由于较高的中断时效温度和较长的中断时间能获得高密度的晶内析出相和呈球状不连续分布的晶界析出相,因此,T6I6时效处理后的6061铝合金不仅能保持较高强度,同时还能显著提高晶间腐蚀抗力.经......
]. In addition, CHEN et al [17] indicated that an ideal semisolid microstructure with small and spheroidal primary particles could be obtained after the 6061 bulk alloy prepared by cold-pressing the atomized...): 1459-1467. 工艺参数对触变模锻6061 Al合金微观组织与力学性能的影响 陈玉狮,陈体军,张素卿,李普博 兰州理工大学 有色金属先进加工与再利用国家重点实验室,兰州730050 摘 要:提出一种制备颗粒增强金属基复合材料的新技术-粉末触变成形, 并利用该技术对基体6061铝合金进行触变模锻.首先,将雾化的6061合金粉末冷压成块,压出的块体作为初始锭料,经部分重熔后再进行触变模锻.研究重熔......
: 6061 Al alloy; aluminum matrix composite; compocasting; rice husk ash; microstructure 1 Introduction The development of aluminum matrix composites (AMCs) is one of the significant milestones...-alumina reinforced Al-Mg-Si alloy matrix hybrid composites [J]. Journal of Materials Research and Technology, 2013, 2: 60-67. [23] ALANEME K K, OLUBAMBI P A. Corrosion and wear behavior of rice husk ash......
: 6061铝合金；温成形；热力拉伸；本构模型；数值仿真 中图分类号: TG146.2 文献标志码:A Thermal constitutive model and numerical simulation of hot forming for 6061-T6 aluminum alloy YING Liang1, 3, DAI Ming-hua2... concentrate softening before crack, which is verified to be effective while applied to numerical simulation of forming process for 6061 aluminum alloy in hot forming. Key words: 6061 Al alloy; hot forming......
者通过对设计的拉伸剪切试样和原位拉伸剪切试样分别进行不同剪应变率下的拉伸剪切试验和原位拉伸剪切试验,研究6061铝合金在不同剪应变率下的力学性能和断裂行为,并对6061铝合金剪切断裂行为进行有限元模拟. 1 实验 1.1 实验材料 试验所用的材料为Al-Mg-Si-Cu系挤压6061铝合金方管(T6态),其室温下的屈服强度为274.8 MPa,抗拉强度为297.9 MPa.该材料的显微组织如图1所示,材料中各元素的含量如表1所列. 表1 挤压6061铝合金的组分 Table 1 Compositions of extrusion 6061 aluminum alloy (mass fraction, %) 图1 挤压6061铝合金的微观组织 Fig. 1 Microstructure of extrusion......
. (in Chinese) [18] WANG Zhu-tang, TIAN Rong-zhang. Handbook of aluminum alloy and processing [M]. Changsha: Central South University of Technology Press, 1988: 1015-1017. (in Chinese). 6061铝合金在线淬火温度场...Trans. Nonferrous Met. Soc. China 24(2014) 2168-2173 Simulation of temperature and stress in 6061 aluminum alloy during online quenching process Meng-jun WANG1,2, Gang YANG, Chang-qing HUANG2, Bin......
and electrical resistivity of Al-Mg-Si balanced alloy: A correlation study[J]. Materials Science and Engineering A, 2008, 465(1/2): 274-282. [10] 杜 鹏, 李彦利, 闺晓东, 沈 健, 张智慧. 高品质6061铝合金均匀化工艺研究[J]. 中国有色金属学报...文章编号:1004-0609(2011)07-1521-06 硬质相对6061铝合金异型散热型材表面质量的影响 罗 淞1, 2, 林高用1, 曾菊花1, 孙利平1 , 邹艳明1, 周玉雄1 (1. 中南大学 材料科学与工程学院,长沙 410083；2. 山西阳泉铝业股份有限公司,阳泉 045003) 摘 要:采用化学成分分析,金相分析,扫描电镜,力学性能测试,能谱......