共搜索到189条信息，每页显示10条信息，共19页。用时：0小时0分0秒694毫秒
): 25-30. [15] JORGE A, AMBROSIO J A C. Material strain rate sensitivity[M]. Crashworthiness, Vienna: Springer, 2001: 33-47. [16] 韦莉莉, 潘清林, 周坚, 等. Al-Zn-Mg-Cu-Zr合金加工图的构建及失稳分析[J]. 中南大学学报(自然科学版), 2013, 44(5): 1798-1804. WEI Lili, PAN Qinglin, ZHOU Jian, et al. Processing maps and flow instability analysis of Al-Zn-Mg-Cu-Zr alloy[J]. Journal of Central South University (Science and Technology), 2013, 44......
[J]. Materials and Manufacturing Processes, 2010, 25(8): 777-785. [6] 刘 斌, 汪明朴, 雷 前, 段雨露, 刘林贤, 虞红春. 喷射沉积法制备Al-Zn-Mg-Cu-Zr合金的显微组织与性能[J]. 中国有色金属学报, 2015, 25(7): 1773-1780.LIU Bin, WANG Ming-pu, LEI Qian, DUAN Yu-lu, LIU Lin-xian, YU Hong-chun. Microstructure and properties of Al-Zn-Mg-Cu-Zr alloy prepared by spray deposition method[J]. The Chinese Journal of Nonferrous Metals, 2015, 25(7......
): 1883-1892. [18] 韦莉莉, 潘清林, 周坚, 等. Al-Zn-Mg-Cu-Zr合金加工图的构建及失稳分析[J]. 中南大学学报(自然科学版), 2013, 44(5): 1798-1804. WEI Lili, PAN Qinglin, ZHOU Jian, et al. Processing maps and flow instability analysis of Al-Zn-Mg-Cu-Zr alloy[J]. Journal of Central South University (Science and Technology), 2013, 44(5): 1798-1804. [19] QUAN Guozheng, WANG Yang, YU Chuntang, et al. Hot workability characteristics......
DOI: 10.11817/j.issn.1672-7207.2017.12.006 微量Si和Fe对Al-Zn-Mg-Cu-Zr-Cr-Ti合金组织与性能的影响 周泽宇,陈康华,许杰,董朋轩 (中南大学 粉末冶金国家重点实验室,湖南 长沙,410083) 摘要:为了提高Al-Zn-Mg-Cu合金的力学性能及抗腐蚀性能,通过拉伸试验,晶间腐蚀,剥落腐蚀,应力腐蚀及电化学试验,并结合金相分析及高分辨电镜分析,研究微量Si和Fe的添加对Al-Zn-Mg-Cu-Zr-Cr-Ti合金组织与性能的影响.研究结果表明:微量元素的添加明显抑制合金的再结晶,使合金晶粒细小,亚结构稳定,强化合金,从而提高其力学性能及抗腐蚀性能,电化学循环极化曲线试验中自腐蚀电流密度的降低也与抗晶间腐蚀能力增强的结果较吻合；复合添加微量Si和Fe元素使合金基体中形成大量粗大黑色的Al7Cu2Fe相,与基体不共格,导致合金时......
了均匀化Al-Zn-Mg-Cu-Zr的动态再结晶和动态回复区域.WU等[15]则通过DMM热加工图研究了Al-Zn-Mg-Er-Zr的动态回复区域和失稳区.然而,DMM的变形历史依赖性被忽略,可能是DMM存在的问题.极化互惠模型(PRM)则将变形历史这一因素考虑在内,同时将材料的速率依赖性作为主要特征来构建加工图,PRM热加工图的一大特点为失稳区与合理加工区充分分开,因此,在钛合金的加工中得到很好的应用[16]. 本文作者研究喷射成形Al-Zn-Mg-Cu-Zr合金在不同加工条件下的热变形行为,结合DMM和PRM加工图,通过组织观察,确定两种加工图与软化机制和失稳行为的关系,以期确定合适的加工工艺,避免该合金在热加工过程中发生失稳行为. 1 实验 1.1 实验材料 实验所用合金是由江苏豪然喷射成形有限公司制备,其实际成分为......
of rapidly solidified Al-20Si alloy powders[J]. Materials Science & Engineering A, 2001, 304(1): 617-620. [7] 丁永根, 王薄笑天, 李 萍, 薛克敏. 高压扭转变形的Al-Zn-Mg-Cu-Zr合金显微组织及织构[J]. 中国有色金属学报, 2017, 27(6): 1125-1131. DING Yong-gen, WANG Bo Xiao-tian, LI Ping, XUE Ke-min. Microstructures and textures of Al-Zn-Mg-Cu-Zr alloy after high pressure torsion[J]. The Chinese Journal of Nonferrous Metals, 2017, 27(6......
-Cu-Zr 合金组织性能和断裂行为的研究[D]. 哈尔滨: 哈尔滨工业大学, 2007: 73-74.FAN Xi-gang. Study on the microstructures and mechanical properties and the fracture behavior of the Al-Zn-Mg-Cu-Zr alloy[D]. Harbin: Harbin... precipitates are η and η' phases, and with minous GPⅡ zone. Key words: 1973 aluminum alloy; two-stage ageing; conductivity; precipitation Al-Zn-Mg-Cu系合金是高强铝合金,由于它具有高的比强度和硬度,易于加工,较好的耐腐蚀性和较高的韧性等特点,被广泛应用于......
]. Changsha: Central South University Press, 2007: 1-581. [6] SENKOV O N, SHAGIEV M R, SENKOVA S V, MIRACLE D B. Precipitation of Al3(Sc,Zr) particles in an Al-Zn-Mg-Cu-Sc-Zr alloy during conventional..., SCAMANS G. Corrosion behavior of friction stir welded AA7108-T79 aluminium alloy[J]. Corrosion Science, 2006, 48(4): 887-897. [24] 张 茁, 陈康华, 方华婵. 微量Cr和Nb对Al-Zn-Mg-Cu-Zr合金力学性能和应力腐蚀性能的影响[J]. 中国有色金属学报, 2008......
DOI: 10.11817/j.issn.1672-7207.2016.02.010 复合添加Zr,Ti和Cr对Al-Zn-Mg-Cu超强合金组织与性能的影响 方华婵1,巢宏2,张茁1,陈康华1 (1. 中南大学 粉末冶金国家重点实验室,湖南 长沙,410083； 2. 湖南省科学技术信息研究所,湖南 长沙,410001) 摘要:采用铸锭冶金法制备Al-Zn-Mg-Cu-Zr-Ti和Al-Zn-Mg-Cu-Zr-Ti-Cr合金.通过金相显微镜,扫描电镜和透射电镜观察和硬度,力学,腐蚀性能测试,对比复合添加Zr和Ti的合金及复合添加Zr,Ti和Cr对Al-Zn-Mg-Cu合金组织和性能的影响.研究结果表明:在Al-Zn-Mg-Cu合金中复合添加Zr,Ti和Cr形成的大量10~20 nm共格的固溶部分Zn,Mg和Cu的(Al,Cr)3(Zr,Ti)弥散相,这些弥散相强烈钉扎位错和亚晶界；与复......
): 74-78. [10] 陈康华, 方华婵, 齐雄伟, 张 茁. 微量 Yb 对 Al-Zn-Mg-Cu-Zr 超高强铝合金的强韧化作用[J]. 中南大学学报(自然科学版), 2008, 39(4): 712-717. CHEN Kang-hua, FANG Hua-chan, QI Xiong-wei, ZHANG Zhuo. Effect of addition of Yb on strength and toughness of Al-Zn-Mg-Cu-Zr high-strength aluminum alloy[J]. J Cent South University (Science and Technology), 2008, 39(4): 712-717. [11] 孙擎擎, 孙睿吉, 陈送义, 陈启元, 陈康华. 大气污染物对7B50铝合金电化学腐蚀性能的影......