of the coating condition on the tensile strength and microstructure were discussed. The results show that the CETs of the borate glass at different temperatures match with those of Ti-based alloy.... With the increase of coating time, the tensile strength of coats increases firstly while then decreases. The coat prepared at 730 ℃ for 30 min is fairly smooth and complete, while the other coats contain lots......
Aspects of Characterisation of Thin Coating Adhesion at the Nano-Scale Jisheng E1,Ben D.Beake2,Aiyang Zhang1 (1.Vitality Z&E Limited, 3 College View ,Tettenhall ,Wolverhampton ,West Midlands ,WV6... coating adhesion on a nano-scale becomes one of the most important research areas,as new coatings get ever thinner and more technologically advanced. With a review of technology and mechanisms......
Oxidation resistance of co-deposited Ni-SiC nanocomposite coating ZHOU Yue-bo(周月波), DING Yuan-zhu(丁元柱) Department of Materials Science and Engineering, Heilongjiang Institute of Science...) nanocomposite coating was prepared from a nickel sulfate bath by co-electrodeposition of Ni and SiC nanoparticles in an average size of 30 nm. The oxidation at 1 000 ℃ shows that the Ni-6.0%SiC......
......
Characterization of self-assembled nano-phase silane-based particle coating SHI Hong-wei(史洪微), LIU Fu-chun(刘福春), HAN En-hou(韩恩厚) State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China Received 22 October 2009; accepted 8 April 2010 Abstract: Self-assembled nano-phase silane-based particle coating......
......
Organic-magnesium complex conversion coating on AZ91D magnesium alloy CHEN Xiao-ming(陈晓明)1, 2, LI Guang-yu(李光玉)1, 2, LIAN Jian-she(连建设)1, 2 1. Key Laboratory of Automobile Materials... 2010 Abstract: An organic-magnesium complex conversion (OMCC) coating on AZ91D magnesium alloy was obtained by treating in a solution containing organic compounds. SEM, FESEM and XPS were used......
of C/C-ZrC-Cu campsite 图5 等离子喷涂W涂层表面SEM像 Fig. 5 SEM image of W coating surface 图6(a)所示为C/C-ZrC-Cu复合材料等离子喷涂W横截面形貌.由图6(a)可见,涂层厚度约为1.3 mm,涂层表面有孔隙,涂层和基体结合处在低倍SEM观察下并没有看到扩散层,有少量的Cu向涂层内渗透以及部分涂... D, CHEN Z K, SUN W, WANG Y L. Ablation behavior of ZrB2-SiC protective coating for carbon/carbon composites[J]. Ceramics International, 2015, 41(6): 7677-7686. [8] ZHOU W Y, YI M Y, PENG K, RAN L P......
......
Forming limits of nickel coating on right region ZHOU Li-qun(周里群)1, 2, LI Yu-ping(李玉平)1, ZHOU Yi-chun(周益春)2 1. School of Mechanical Engineering, Xiangtan University, Xiangtan 411105, China; 2... of nickel coating on the right region were studied, so as to direct the preparation of the material and help the production of workpieces. The electrodeposited nickel coating was prepared on steel......