共搜索到18632条信息,每页显示10条信息,共1864页。用时:0小时0分0秒296毫秒
Trans. Nonferrous Met. Soc. China 23(2013) 699-710 Effect of fluoride treatment on corrosion behavior of Mg-Ca binary alloy for implant application Hamid Reza Bakhsheshi-Rad1, Mohd Hasbullah Idris1... and delamination. Fluoride treated Mg-0.5Ca alloy with 40% HF is a promising candidate as biodegradable implants due to its low degradation kinetics and good biocompatibility. Key words: Mg-Ca alloy......
Trans. Nonferrous Met. Soc. China 25(2015) 3339-3347 Corrosion degradation behavior of Mg-Ca alloy with high Ca content in SBF Yi-chi LIU1, De-bao LIU1, Yue ZHAO1,2, Min-fang CHEN1 1. School..., University of Wollongong, Northfield Ave, Wollongong, NSW 2522, Australia Received 27 November 2014; accepted 25 March 2015 Abstract: The corrosion degradation behavior of a Mg-Ca alloy with high Ca......
Trans. Nonferrous Met. Soc. China 31(2021) 1612-1627 In-situ layered double hydroxides on Mg-Ca alloy: Role of calcium in magnesium alloy Yu XIA1, Liang WU1,2, Wen-hui YAO1,2, Meng HAO1, Jing CHEN1... Schematic diagrams illustrating alloy melting (a) and preparation of LDHs by in-situ growth method (b) The Mg-Ca alloys were cut into specimens with size of 10 mm × 10 mm × 3 mm and 20 mm × 20 mm × 3......
investigated using optical microscope, scanning electron microscope and transmission electron microscopes.The as-cast Mg-Ca alloy containing only Ca is composed of Mg matrix and divorced eutectic (Mg+Mg2Ca) formed along the grain boundaries. With about 0.5%Si (mass fraction) added to the Mg-Ca alloy to produce Mg-Ca-Si alloys, no grain boundary divorced eutectic is formed any more, instead......
梯度多孔Mg-Ca合金的力学性能研究李强1,2,张峰峰1,于景媛1,周旭1,孙旭东21. 辽宁工业大学材料科学与工程学院2. 东北大学材料与冶金学院摘 要:主要研究了具有不同孔隙梯度分布的多孔Mg-Ca合金在横向和纵向压缩时孔洞的受力以及变形特征,分析了梯度多孔Mg-Ca合金在弯曲时裂纹扩展机理,并观察了孔隙梯度结构和烧结温度对梯度多孔Mg-Ca合金力学性能的影响.研究结果表明,梯度多孔Mg-Ca合金的力学性能优于均匀多孔材料,随着试样边缘和中心孔隙度差距的增加,试样的抗弯强度,抗压强度和弹性模量均增加,纵向压缩时样品抗压强度和弹性模量的增加优于横向压缩,这主要归因于孔隙的梯度分布导致受力时外加载荷的重新分配.随着烧结温度增加,梯度多孔Mg-Ca合金的力学性能增加,在620℃烧结2h时力学性能达到最佳......
, indicating that the obtained micro arc coatings achieve excellent bioactivity. Key words: Mg-Ca alloy; micro arc oxidation; calcium phosphate coating; corrosion degradation 镁合金具有弹性模量低,密度与人骨接近以及可体内降解等优点,成为可降...% Mg和1.0% Ca(质量分数),试样规格为d 50 mm×10 mm的圆柱状.分别采用180~1000号的水砂纸由粗到细逐级打磨,然后经蒸馏水清洗,无水乙醇擦洗,热风吹干后,置入干燥器中待用.使用的电解液为3 g/L氢氧化钠,15 g/L植酸钠和5 g/L CaCO3.采用国产MAOI-50C微弧氧化电源,使用单(正)脉冲恒流控制,电参数如下:电流密度为40 mA/cm2,占空比为35%,频率为......
超声波施振参数对Mg-Ca合金除气的影响贾征,乐启炽,张志强,崔建忠东北大学材料电磁过程研究教育部重点实验室摘 要:采用了超声场来处理Mg-Ca合金熔体,考察了超声波施振参数(超声功率和作用时间)对合金熔体除气效果的影响.结果表明:超声波施振功率和作用时间均对Mg-Ca合金除气效果有较大的影响,当施振功率过小,作用时间过短或过长均不会有良好的除气效果.这种除气效果和超声波的空化效应有关,且只有在空化效应的发展-发达阶段才会有良好的除气效果.在本实验条件下,超声功率150 W,作用时间为120 s除气效果最好,铸锭的密度值达到最大.在除气的同时,也有效地细化了Mg-Ca合金铸锭的凝固组织.关键词:Mg-Ca合金;超声场;除气;细化;空化效应;......
ZLX-1600型离子交换设备的研制 曾毅君1,雷泽勇2,钟平汝1 (1.核工业北京化工冶金研究院,北京,101149;2.南华大学科技处,湖南,衡阳,421001) 摘要:研制的ZLX-1600型固定床离子交换塔可在流速≤40 m/h范围内操作,适应不同的进料流量和铀浓度.采用密闭顺流连续操作方式,处理量大,操作简单,运行平稳,树脂不需转移,损耗少.独特的减阻防冲击进液结构设计保持树脂床层稳定,创新的出液装置结构保证了出液顺畅. 关键词:铀; 离子交换设备; 研制; [全文内容正在添加中] ......
Localized Corrosion of Binary Mg-Ca Alloy in 0.9 wt%Sodium Chloride SolutionRui-Qing Hou1,Chen-Qing Ye2,Cheng-Dong Chen1,Shi-Gang Dong3,Miao-Qiang Lv1,Shu Zhang1,Jin-Shan Pan4,Guang-Ling Song5,Chang... used to monitor the corrosion process of Mg-l.OCa alloy in0.9 wt%sodium chloride solution.The results indicated that the localized corrosion was accompanied by the formation and thickening......
Mg-Ca合金中添加Al对G.P.区形成的影响钱一辰1,2,袁蓉1,2,马海涛1,2,谢耀平1,2,胡丽娟1,21. 上海大学材料科学与工程学院材料研究所2. 上海大学微结构重点试验室摘 要:Mg-Ca合金在时效峰值时的主要析出强化相为G. P.区,因此研究合金元素对G. P.区稳定性的影响具有重要意义.采用第一性原理方法研究了Mg-Ca合金中添加Al对G. P.区稳定性的影响.结果表明,Al的添加能显著降低Mg-Ca合金中G. P.区的形成能,说明Al能促进该合金中G. P.区的析出,增加其密度,从而有效提升该合金的时效硬化效果,这与相关文献的试验结果一致.此外,研究还发现,G. P.区惯析面的晶体取向与其溶质成分有着较强的依赖关系.最后,通过电子结构分析进一步在原子层次上揭示了Al促进G. P.区......