共搜索到22434条信息,每页显示10条信息,共2244页。用时:0小时0分0秒515毫秒
Received 21 November 2016; accepted 6 March 2017 Abstract: Severe surface roughening during plastic deforming of aluminum alloy parts can produce "orange peel" defects. To analyze "orange peel" of 6063..., and was aggravated as the grain size increased due to the larger local deformation in larger grains. Key words: 6063 aluminum alloy; surface roughening; tensile deformation; spinning; orange peel 1 Introduction......
both simulations and experiments to the forming process of the helical surface, of which the material is 6063 aluminum alloy. The forward hot extrusion process is simulated with finite element method... and significant effect on the increment of twist angle. Therefore, the twist angle has an increase of about 76%, which verifies the modified die structure. Key words: 6063 aluminum alloy; helical......
Trans. Nonferrous Met. Soc. China 27(2017) 1498-1506 Influence of heat treatment conditions on bending characteristics of 6063 aluminum alloy sheets Zhi-wen LIU1,2, Luo-xing LI1,2, Jie YI1, Shi-kang... deformation behaviors of solution treated (ST), natural aged (NA) and T6 tempered 6063 aluminum alloy sheets were studied by three-point bending tests. The changes of bending force, interior angle, bending......
Trans. Nonferrous Met. Soc. China 23(2013) 38-45 Time-temperature-property curves for quench sensitivity of 6063 aluminum alloy Hong-ying LI1,2, Cui-ting ZENG1, Mao-sheng HAN1, Jiao-jiao LIU1, Xiao... the residual stress. Key words: 6063 aluminum alloy; quench sensitivity; hardness; time-temperature-property curve; strengthening phase; heterogeneous precipitation; residual stress 1 Introduction 6063......
......
South University, Changsha 410083, China; 3. Changsha New Zhensheng Group Co. Ltd, Changsha 410100, China) Abstract: A new type of Al-Mg-Si alloy was designed based on 6063 alloy. After extrusion... analyzed with optical microscope, X-ray diffractrometry, scanning electron microscopy and electronic testing machine. The results show that compared with 6063 alloy, the new alloy has a higher strength......
? tensile test and 90? tensile test respectively. The simulated engineering stress-engineering strain curves fit the measured ones very well. Key words: 6063 aluminum alloy; damage mechanism.... The damage forms on the 6063 aluminum alloy under crushing loading are changing with the changing of stress states. So any one-damage model can’t describe adequately the damage and deformation forms......
Trans. Nonferrous Met. Soc. China 26(2016) 806-813 Effects of current density on microstructure and properties of plasma electrolytic oxidation ceramic coatings formed on 6063 aluminum alloy Nan... connected with morphologies of coatings. Key words: 6063 aluminum alloy; ceramic coating; plasma electrolytic oxidation (PEO); current density; microstructure; mechanical property 1 Introduction......
were evaluated through finite element method (FEM). 2 Experimental Commercial 6063 aluminum alloy was adopted in this study. Diameters of billets and the extrusion wheel are 9.5 and 350 mm, respectively... after extrusion and then artificial aging treatment was applied at 200 °C for 2 h. Experiments were conducted to analyze weld seams of the 6063 aluminum alloy under various extrusion wheel rotational......
deviation is 0.28 mm. Both the thickness distribution and dimensional accuracy meet the design requirements. Key words: 6063 aluminum; hydroforming; thickness distribution; size deviation 近年来,为了实现汽车节能减排,降低污...材的真应力-应变曲线如图1所示.表1所列为管材力学性能参数,其中σs为屈服强度;σb为抗拉强度;δ为断后伸长率;n为硬化指数;K为强度系数. 图1 6063-T4管材的真应力-应变曲线 Fig. 1 Stress-strain curve of aluminum alloy 6063-T4 tube 表1 6063-T4管材力学性能 Table 1  ......