Trans. Nonferrous Met. Soc. China 25(2015) 2253-2259
Synthesis of Ni0.8Co0.1Mn0.1(OH)2 precursor and electrochemical performance of LiNi0.8Co0.1Mn0.1O2 cathode material for lithium batteries
Yue HUANG, Zhi-xing WANG, Xin-hai LI, Hua-jun GUO, Jie-xi WANG
School of Metallurgy and Environment, Central South University, Changsha 410083, China
Received 2 September 2014; accepted 3 March 2015
Abstract:
Spherical and homogeneously mixed metal hydroxide Ni0.8Co0.1Mn0.1(OH)2 precursor was successfully synthesized by co-precipitation method in a simple and small vessel with the volume of 1 L. The conditions of synthetic process including amount of chelating agent, stirring speed and temperature were studied. LiNi0.8Co0.1Mn0.1O2 samples were obtained by calcinating the precursors. The crystal structure, morphology and electrochemical properties were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), charge-discharge test, AC impedance and cyclic voltammetry. In the voltage range of 2.8-4.3 V, the initial discharge capacities of LiNi0.8Co0.1Mn0.1O2 at 0.1C and 1C rates were 199 and 170 mA·h/g, respectively. After 80 cycles at 1C, the discharge capacity retention was 92%, suggesting its promising application as the cathode material for Li-ion batteries.
Key words:
lithium-ion batteries; cathode material; co-precipitation; electrochemical properties;
1 Introduction
Layered LiNi1-x-yCoxMnyO2(LNCM) exhibits high capacity, good cycling stability and low cost, and has been considered to be a promising cathode material for automobile applications such as plug-in hybrid vehicles (PHEVs) and electric vehicles (EVs) [1–3].{Shim, 2002 #248} Among these layered materials, LiNi0.8Co0.1Mn0.1O2 shows a relatively high capacity than LiNi1/3Co1/3Mn1/3O2 and LiNi0.6Co0.2- Mn0.2O2 due to the high content of Ni which is the main active redox species (Ni2+
Ni4+) in the host structure [4-6].
Great efforts have been made toward the synthesis of Ni-rich materials [7,8]. Previous work proved that it is difficult to prepare high amount of Ni contented compounds, partly due to the sensitivity to synthesis condition. The synthesis process needs to be operated under stable environment with precise control, and there have been some reports that high Ni-content spherical material can be successfully synthesized by using adjusted reactors with large capacity [9,10]. However, there is no report that high Ni-content spherical composite materials with good performance can be synthesized by using simple and small reactors.
In this work, high Ni-content precursors were synthesized in a relatively simple and small reactor with capacity of about 1 L. The synthesis conditions including stirring speed, temperature and amount of chelating agent have been investigated. After co- precipitation, spherical and homogeneously mixed metal hydroxide Ni0.8Co0.1Mn0.1(OH)2 were successfully synthesized. Then LiNi0.8Co0.1Mn0.1O2 with good electrochemical performance was synthesized from the precursor by calcination under oxygen atmosphere.
2 Experimental
2.1 Sample preparations
The progress of preparing Ni0.8Co0.1Mn0.1(OH)2 is graphically presented in Fig. 1. NiSO4·6H2O, CoSO4·7H2O and MnSO4·H2O were used as starting materials and were dissolved in distilled water in a mole ratio of n(Ni2+):n(Co2+):n(Mn2+)=8:1:1, and the total metal ions concentration is 1 mol/L. Subsequently, this solution was slowly pumped into a reactor (1 L) with continuous stirring under nitrogen atmosphere. Simultaneously, a 2 mol/L NaOH solution and an appropriate amount of NH4OH solution as chelating agent were also pumped into the reactor together. After that, the precipitate was filtered and washed several times with distilled water to remove the residual ions (Na+, 
and other ions). The precipitate was then dried at 80 °C overnight. The concentration of the solution, pH (the pH value was controlled at 11.25), the amount of NH4OH, stirring speed and temperature in the reactor were carefully controlled. The obtained Ni0.8Co0.1Mn0.1- (OH)2 precursor was mixed with LiOH·H2O in a mole ratio of 1:1.05 and thoroughly ground. Then, the mixture was sintered at 480 °C for 5 h followed by at 750 °C for 15 h in flowing oxygen atmosphere.
Fig. 1 Experimental procedure and apparatus
2.2 Sample characterization
X-ray diffraction (XRD) was carried out with a diffractometer D/max 2550 X (Rigaku, Japan), using Cu Kα radiation (λ=0.154056 nm, voltage 40 kV, and current 300 mA), with a step size of 0.02° and a recorded range from 10° to 80°. The SEM images and elemental mapping of the particles were observed with scanning electron microscope (SEM, JEOL, JSM-5600LV).
2.3 Electrochemical performance evaluation
The electrodes for electrochemical studies were fabricated from a mixture of the active material, super P and poly(vinylindene fluoride) at a mass ratio of 8:1:1. The mixture was dispersed in N-methyl pyrrolidinone (NMP) and stirred to form viscous slurry, which was then coated onto Al foil using a doctor-blade. After drying at 120 °C for 12 h, the film was punched into disks with a diameter of 12 mm. Then, the disks were vacuum dried at 60 °C for 12 h, cooled and transferred into an argon-filled glove-box, followed by being assembled into CR2025 coin-type cells with a negative electrode of Li foil and electrolyte (1 mol/L LiPF6 in m(EC):m(EMC):m(DMC)=1:1:1). The charge–discharge tests were implemented between 2.8 and 4.3 V at a desired rate (1C corresponds to 200 mA/g). Before cycling tests, all the cells were sequentially activated at 0.1C , 0.2C and 0.5C for two cycles, respectively, and then cycled at 1C rate in the following 100 cycles at 25 °C. Cyclic voltammogram (CV) measurements were done by a CHI660A electrochemical workstation between 2.8 and 4.3 V at a scan rate of 0.1 mV/s. AC impedance was tested on the same electrochemical workstation over the frequency range of 0.01 Hz to 100 kHz.
3 Results and discussion
3.1 Optimization of synthetic conditions of Ni0.8Co0.1Mn0.1(OH)2
The spherical Ni0.8Co0.1Mn0.1(OH)2 precursor with a very homogeneous distribution of Ni2+, Co2+ and Mn2+ on the atomic scale can be synthesized via the co-precipitation method [9,11-14]. And it is easier to synthesize LiNi0.8Co0.1Mn0.1O2 from Ni0.8Co0.1Mn0.1- (OH)2 precursor because they share very similar layered structure which has been indicated by the X-ray diffraction patterns [6,12]. During the synthetic process, the pH, stirring speed, temperature and amount of chelating agent are crucial factors [11–14]. In this research, series of experiments were operated by changing three critical factors including different concentrations of NH4OH, stirring speeds and temperatures. And five representative experiments were picked out and listed in Table 1 to illustrate the effects of synthesis conditions on the physical and electrochemical properties of the cathodes. Ni0.8Co0.1Mn0.1(OH)2 samples which were prepared under different conditions were labeled as Si(i=1, 2, 3, 4, 5).
Table 1 Preparation conditions of Ni0.8Co0.1Mn0.1(OH)2 powders
The pH value might change the composition of materials by affecting the formation of manganese compounds [15,16]. For example, excess of alkali during precipitation reaction facilitates the formation of some kinds of manganese oxides, so the pH value plays an important role to decide the purity of metal hydroxide [9]. Based on the former experiments (which are not shown here), the value of pH is 11.25 [12].
Figure 2 shows the SEM images of the Ni0.8Co0.1Mn0.1(OH)2 powders of S1, S2, S3, S4 and S5, prepared at different conditions listed in Table 1.
Speeding up stirring rate can intensify the collision not only between the particles themselves but also between the particles and the vessel wall. That is beneficial to forming uniform and homogeneous spherical particles. Compared with sample S1, sample S2 was prepared at higher stirring speed (700 r/min), which suppressed the irregular agglomeration of the particles.
It is well known that NH3 molecules play an important role on promoting the formation of Ni0.8Co0.1Mn0.1(OH)2 powders. Single phases of Ni(OH)2, Co(OH)2 or Mn(OH)2 would form and exist as impurity phase in the final product if the chelating agent of NH4OH was not employed [17]. Samples S1 and S3 were prepared with different concentrations of NH4OH as described in Table 1. With a low concentration of NH4OH (see S1), irregular particles result in serious agglomeration due to the existence of a lot of vacancies among particles and the bad fluidity of the powders. With a higher concentration of NH4OH (sample S3), the particles become homogenous, small and quasi-spherical.
High temperature is beneficial for the formation of Mn contained hydroxide, however, when the temperature is higher than 60 °C, Mn(OH)2 tends to be oxidized to MnO(OH) [9]. The SEM images of the samples S3 and S4 show that comparatively higher temperature facilitates the growth of secondary particles. As shown in Fig. 2, sample S5 prepared with higher temperature (58 °C), higher stirring speed (800 r/min) and high concentration of NH4OH (2 mol/L) exhibits more uniform morphology. Under this condition, the particles are nearly spherical in shape. This result is consistent with the previous studies, that relatively high temperature and stirring speed with appropriate amount of NH4OH and value of pH facilitate the formation of uniform and spherical particles [9,10,12].
Fig. 2 SEM images of Ni0.8Co0.1Mn0.1(OH)2 powders prepared at different conditions
3.2 Preparation of LiNi0.8Co0.1Mn0.1O2
Figure 3 displays the XRD patterns of the five LiNi0.8Co0.1Mn0.1O2 samples synthesized from the precursors Si (i=1, 2, 3, 4, 5). LiNi0.8Co0.1Mn0.1O2 samples were labelled as 
(i=1, 2, 3, 4, 5) in order to distinguish from the corresponding precursors. The results reveal that all peaks are indexed as hexagonal a-NaFeO2 structure with a space group of 
and no extra diffraction peaks exist. As can be seen, all the XRD patterns show clear splits between the 006/012 and 108/110 peaks, which means that the materials have obvious hexagonal structure [6,18].
Fig. 3 XRD patterns for LiNi0.8Co0.1Mn0.1O2 samples prepared at 750 °C
3.3 Electrochemical properties of LiNi0.8Co0.1Mn0.1O2 materials
Figure 4(a) exhibits the initial charge–discharge curves of the synthesized LiNi0.8Co0.1Mn0.1O2 samples at a current density of 0.1C at room temperature. All the cells show very smooth curves. However, different samples deliver different discharge capacities. The initial discharge capacities for sample 
to 
are 174, 164, 180, 187, and 199 mA·h/g, respectively. And the corresponding coulombic efficiencies are 78%, 81%, 82%, 87% and 86%, respectively.
Figure 4(b) presents the cycle performance of the obtained LiNi0.8Co0.1Mn0.1O2 samples at 1C at room temperature. The discharge capacities of all the samples tend to decrease slowly with the increase of the cycle number. The capacity retentions for samples to are 94%, 95%, 93%, 89% and 92% after 80 cycles, respectively. Sample 
exhibits the highest capacity retention but low initial capacity. Considering both capacity and capacity retention rate, sample owns better electrochemical performance than the others.
Fig. 4 Initial charge–discharge curves (a) and discharge capacities as function of number of cycle (b) in voltage range of 2.8–4.3 V at 1C rate at 25 °C of LiNi0.8Co0.1Mn0.1O2
Here, sample was picked up to examine the composition and the uniformity on the surface of the particles by using energy dispersive X-ray spectroscopy (EDX). It is seen from Fig. 5 that the Ni, Co and Mn elements are uniformly distributed on the particles’ surface. Moreover, it can be found that the spherical shape and the size of secondary particle are maintained after calcination (Fig. 5(b)). The mole ratio of n(Ni):n(Co): n(Mn) is nearly 8:1:1, which is consistent with the initial designed composition. The result also proves that homogeneously mixed metal hydroxide Ni0.8Co0.1Mn0.1(OH)2 is synthesized.
Figure 6 shows the rate capacity of sample between the voltage of 2.8-4.3 V. The cell was cycled at 0.1C 0.2C, 0.5C, 1C, 2C and 5C rates sequentially with 10 cycles for each current density. The cell delivers discharge capacities of 196, 185, 175, 163, 152 and 127 mA·h/g at 0.1C, 0.2C, 0.5C, 1C, 2C and 5C rates, respectively. As seen in Fig. 6(b), after being cycled at 5C, the capacity shows no capacity fading when the current density was back to 0.1C.
Electrochemical impedance spectroscopy (EIS) was measured after different cycles at charge state (Fig. 7(a)). The Nyquist plots are fitted using the equivalent circuit model (inset Fig. 7(a)) and the fitting parameters are listed in Table 2. Rsf stands for surface film impedance and Rct stands for electrolyte/oxide reaction resistance. This model includes the Ohmic resistance (Re) of the cell, the surface film impedance (Rsf//CPEsf), electrolyte/oxide reaction resistance (Rct//CPEdl), and the Warburg impedance (Zw). Table 2 shows that the surface film resistance is nearly stable and electrolyte/oxide reaction resistance gradually increases upon further cycling. The stability of Rsf is due to the stable solid-electrolyte interface (SEI) film which was formed on the surface of the electrode after activation. The subsequent continuous increasing in Rct confirms that the impedance increases slowly with the increasing of cycles.
Cyclic voltammetries of the sample between 2.8 and 4.3 V at a scan rate of 0.1 mV/s for the first, second and third cycle were carried out to investigate the structural stability of LiNi0.8Co0.1Mn0.1O2, as shown in Fig. 7(b). It can be seen that three redox couples exist in the cyclic voltammogram curves, a sharp oxidation peak and two secondary peaks, illustrating that phase transitions exist from hexagonal to monoclinic in the voltage range of 2.8–4.3 V [19,20]. It is clearly shown in Fig. 7(b) that the major anodic peak shifts from 3.865 V at the first cycle to 3.793 V and 3.784 V at the second and third cycle, respectively, while their corresponding redox reaction gaps are 0.167, 0.095 and 0.086 V. However, there is no obvious difference in the cathodic peaks (3.698 V). This phenomenon may be partially attributed to the cation mixing in the first cycle [12]. After the first cycle, the curves of the second and third cycle almost overlap. This demonstrates the good reversibility of Li+ ions during intercalating and de-intercalating in compound and the high electrochemical performance.
Fig. 5 EDX spectrum (a), SEM image (b) and elemental mappings (c-f) of sample 
Fig. 6 Charge-discharge curves at different rates (a) and rate capacity curves (b) of sample S5
Fig. 7 Nyquist plots after different cycles (a) and cyclic voltammogram curves (b) of sample
Table 2 Impedance parameters for sample recorded after different cycle numbers
4 Conclusions
1) Spherical and homogeneous Ni0.8Co0.1Mn0.1(OH)2 were successfully synthesized in round bottom flask with four necks (1 L) by co- precipitation method.
2) The as-prepared LiNi0.8Co0.1Mn0.1O2 electrode shows a good cycling stability which exhibits discharge capacity of 199 mA·h/g at a current density of 20 mA/g, and initial discharge capacity of 170 mA·h/g at 1C rate with capacity retention of 92% after 80 cycles, as well as excellent rate capability.
3) These results indicate that high-performance LiNi0.8Co0.1Mn0.1O2 cathode materials can be synthesized in small reactor by co-precipitation method, and this is a simple but efficient synthesis route for high Ni material.
References
[1] Shim J, Kostecki R, Richardson T, Song X, Striebel K. Electrochemical analysis for cycle performance and capacity fading of a lithium-ion battery cycled at elevated temperature [J]. Journal of Power Sources, 2002, 112(1): 222-230.
[2] Belharouak I, Sun Y K, Liu J, Amine K. Li(Ni1/3Co1/3Mn1/3)O2 as a suitable cathode for high power applications [J]. Journal of Power Sources, 2003, 123(2): 247-252.
[3] Yabuuchi N, Ohzuku T. Novel lithium insertion material of LiCo1/3Ni1/3Mn1/3O2 for advanced lithium-ion batteries [J]. Journal of Power Sources, 2003, 119: 171-174.
[4] Cho J, Kim T J, Kim J, Noh M, Park B. Synthesis, thermal, and electrochemical properties of AlPO4-coated LiNi0.8Co0.1Mn0.1O2 cathode materials for a Li-ion cell [J]. Journal of The Electrochemical Society, 2004, 151(11): A1899-A1904.
[5] Kim M H, Shin H S, Shin D, Sun Y K. Synthesis and electrochemical properties of Li[Ni0.8Co0.1Mn0.1]O2 and Li[Ni0.8Co0.2]O2 via co-precipitation [J]. Journal of Power Sources, 2006, 159(2): 1328-1333.
[6] Noh H J, Youn S, Yoon C S, Sun Y K. Comparison of the structural and electrochemical properties of layered Li[NixCoyMnz]O2 (x=1/3, 0.5, 0.6, 0.7, 0.8 and 0.85) cathode material for lithium-ion batteries [J]. Journal of Power Sources, 2013, 233: 121-130.
[7] Sun Bin, Shen Guo-pei, Hu Yan-long. High-rate capability of spinel LiNi0. 05Mn1.95O4 cathode for Li-ion batteries prepared via coprecipitated precursor [J]. Transactions of Nonferrous Metals Society of China, 2007, 17(S1): s937-s940.
[8] Li Ling-jun, Li Xin-hai, Wang Zhi-xing, Wu Ling, Zheng Jun-chao, Li Jin-hui. Synthesis of LiNi0.8Co0.1Mn0.1O2 cathode material by chloride co-precipitation method [J]. Transactions of Nonferrous Metals Society of China, 2010, 20(S1): s279-s282.
[9] Lee M H, Kang Y J, Myung S T, Sun Y K. Synthetic optimization of Li[Ni1/3Co1/3Mn1/3]O2 via co-precipitation [J]. Electrochimica Acta, 2004, 50(4): 939-948.
[10] Liang Long-wei, Du Ke, Peng Zhong-dong, Cao Yan-bing, Duan Jian-guo, Jiang Jian-bing, Hu Guo-rong. Co-precipitation synthesis of Ni0.6CO0.2Mn0.2(OH)2 precursor and characterization of LiNi0.6CO0.2Mn0.2O2 cathode material for secondary lithium batteries [J]. Electrochimica Acta, 2014, 130: 82-89.
[11] Liu Zhao-lin, Yu Ai-shui, Lee J Y. Synthesis and characterization of LiNi1-x-yCoxMnyO2 as the cathode materials of secondary lithium batteries [J]. Journal of Power Sources, 1999, 81: 416-419.
[12] Li Ling-jun, Li Xin-hai, Wang Zhi-xing, Guo Hua-jun, Yue Peng, Chen Wei, Wu Ling. A simple and effective method to synthesize layered LiNi0.8Co0.1Mn0.1O2 cathode materials for lithium ion battery [J]. Powder Technology, 2011, 206(3): 353-357.
[13] PAN Cheng-chi, BANKS C E, SONG Wei-xin, WANG Chi-wei, CHEN Qi-yuan, JI Xiao-bo. Recent development of LiNixCoyMnzO2: Impact of micro/nano structures for imparting improvements in lithium batteries [J]. Transactions of Nonferrous Metals Society of China, 2013, 23(1): 108-119.
[14] HU Chuan-yue, GUO Jun, DU Yong, XU Hong-hui, HE Yue-hui. Effects of synthesis conditions on layered Li[Ni1/3Co1/3Mn1/3]O2 positive-electrode via hydroxide co-precipitation method for lithium-ion batteries [J]. Transactions of Nonferrous Metals Society of China, 2011, 21(1): 114-120.
[15] YU Xiao-yuan, HU Guo-rong, PENG Zhong-dong, XIAO Jin, LIU Ye-xiang. Synthesis and electrochemical characterization of layered Li[Ni1/3Co1/3Mn1/3]O2 cathode material for Li-ion batteries [J]. Transactions of Nonferrous Metals Society of China, 2005, 15(6): 1425-1428.
[16] Zhang Chuan-fu, Yang Ping, Dai Xi, Xiong Xuan, Zhan Jing, Zhang Yin-liang. Synthesis of LiNi1/3Co1/3Mn1/3O2 cathode material via oxalate precursor [J]. Transactions of Nonferrous Metals Society of China, 2009, 19(3): 635-641.
[17] Li De-cheng, Sasaki Y, Kageyama M, Kobayakawa K, Sato Y. Structure, morphology and electrochemical properties of LiNi0.5Mn0.5-xCoxO2 prepared by solid state reaction [J]. Journal of Power Sources, 2005, 148: 85-89.
[18] LI Yan, LIU Kai-yu, 
Mei-yu, WEI Lai, ZHONG Jian-jian. Synthesis, characterization and electrochemical performance of AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 as cathode for Li-ion battery [J]. Transactions of Nonferrous Metals Society of China, 2014, 24(12): 3534-3540.
[19] Li W, Reimers J N, Dahn J R. In situ X-ray diffraction and electrochemical studies of Li1-xNiO2 [J]. Solid State Ionics, 1993, 67(1): 123-130.
[20] WOO S U, YOON C S, AMINE K, BELHAROUAK I, SUN Y K. Significant improvement of electrochemical performance of AlF3-coated Li[Ni0.8Co0.1Mn0.1]O2 cathode materials [J]. Journal of The Electrochemical Society 2007, 154(11): A1005-A1009.
锂离子电池正极材料LiNi0.8Co0.1Mn0.1O2及其前驱体的制备和性能
黄 越，王志兴，李新海，郭华军，王接喜
中南大学 冶金与环境学院，长沙 410083
摘 要：通过共沉淀法在体积为1 L的简易烧杯中合成具有球形形貌的层状前驱体Ni0.8Co0.1Mn0.1(OH)2。探讨合成过程中影响因素，包括络合剂用量、搅拌速度和反应温度对产物形貌和性能的影响。通过高温烧结前驱体合成LiNi0.8Co0.1Mn0.1O2材料。用扫描电子显微镜(SEM)和X射线衍射仪(XRD)对材料的形貌和晶体结构进行表征，通过充放电测试、交流阻抗和循环伏安法研究材料的电化学性能。在2.8-4.3 V电压范围内，合成的LiNi0.8Co0.1Mn0.1O2在0.1C和1C倍率下的首次放电容量分别为199和170 mA·h/g。在1C下循环80次后，其容量保持率为92%，表明这是一种具有良好应用前景的锂离子电池正极材料。
关键词：锂离子电池；正极材料；共沉淀法；电化学性能
(Edited by Yun-bin HE)
Foundation item: Project (2014CB643406) supported by the National Basic Research Program of China
Corresponding author: Zhi-xing WANG; Tel/Fax: +86-731-88836633; E-mail: zxwang@csu.edu.cn
DOI: 10.1016/S1003-6326(15)63838-9
Abstract: Spherical and homogeneously mixed metal hydroxide Ni0.8Co0.1Mn0.1(OH)2 precursor was successfully synthesized by co-precipitation method in a simple and small vessel with the volume of 1 L. The conditions of synthetic process including amount of chelating agent, stirring speed and temperature were studied. LiNi0.8Co0.1Mn0.1O2 samples were obtained by calcinating the precursors. The crystal structure, morphology and electrochemical properties were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), charge-discharge test, AC impedance and cyclic voltammetry. In the voltage range of 2.8-4.3 V, the initial discharge capacities of LiNi0.8Co0.1Mn0.1O2 at 0.1C and 1C rates were 199 and 170 mA·h/g, respectively. After 80 cycles at 1C, the discharge capacity retention was 92%, suggesting its promising application as the cathode material for Li-ion batteries.