Electrical conductivity of MO(MO=FeO, NiO)-containing CaO-MgO-SiO2-Al2O3 slag with low basicity
SUN Chang-yu, GUO Xing-min
School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing, Beijing 100083, China
Received 9 September 2010; accepted 18 December 2010
Abstract:
As a fundamental study on recovery of valuable metals from nonferrous metallurgical slags, electrical conductivity values of MO(MO=FeO, NiO)-containing CaO-MgO-SiO2-Al2O3 slag with a low basicity were measured at different temperatures using AC impedance spectroscopy. The result shows that the electrical conductivity increased from 1.4 S/m to 14.4 S/m with the increase of the temperature from 1 573 to 1 773 K and the content of MO which is less than 12% under the constant mass ratio of (CaO+MgO) to (SiO2+Al2O3) of 0.47. Moreover, the increase magnitude of the electrical conductivity was also promoted with the increase of the content of MO. The electrical conductivity of FeO-containing slags was close to that of NiO-containing slags when the content was less than 8%; however, it was obviously larger than that of NiO-containing slags when the content was 12%. The activation energy of the electrical conductivity decreased with the increase of MO content.
Key words:
FeO; NiO; molten slag; electrical conductivity; AC impedance spectroscopy;
1 Introduction
Recovery of valuable elements from metallurgical slags has been paid considerable attention to the decrease of natural mineral resources for extraction of metals and the increase of the slags at our living environment. In extraction of the valuable metals from the slags, an electrical conductivity is important for understanding the structure of molten slags and optimizing the metallurgical process [1-3]. Indeed, many researches have been conducted on investigating the electrical conductivity of molten slags.
The electrical conductivities of FexO-CaO-SiO2 [4-8], FexO-CaO-MgO-SiO2 [9-10], FexO-CaO-SiO2- Al2O3 [11-12], NixO-CaO-SiO2 [13] and NixO-CaO- MgO-SiO2 [13] slags had been measured and reported in published literature. Normally, the electrical conductivities of those molten slags increased with the increases of temperature and contents of FexO, CaO and MgO. In that, the effect of MgO on the electrical conductivity was proportional to the mass ratio of (FexO+CaO) to SiO2. In addition, KAWAHARA et al [13] reported that a dissociation of NiO into Ni2+ and O2- was promoted after adding MgO into NixO-CaO-SiO2 slags, which resulted in the increase of the electrical conductivity. However, no much work has been performed on investigating the electrical conductivity of MO(MO=FeO,NiO)-CaO-MgO-SiO2-Al2O3 systems like nonferrous metallurgical slags [14-15]. In FexO-CaO- MgO-SiO2-Al2O3 slags, the electrical conductivities of 30% FeO-containing slags at different oxygen partial pressures were measured by HUNDERMARK et al [16], which shows that the electrical conductivity initially increased and then decreased with the increase of the oxygen partial pressure. The effect of the FeO content on the electrical conductivity was investigated by FONTANA et al [17], which shows the activation energy decreased with the increase of the FeO content in a range of 15%-80%. The effect of basicity on the electrical conductivity from 1 673 K to 1 873 K was studied by LUGANOV et al [18], which shows that the electrical conductivity increased with the increase of (CaO+MgO)/ (SiO2+Al2O3) mass ratio. However, the effect of the low FeO and NiO contents on the electrical conductivity of low basicity slag had less been reported.
In this work, the electrical conductivities of MO(MO=FeO, NiO)-CaO-MgO-SiO2-Al2O3 slags with (CaO+MgO)/(SiO2+ Al2O3) mass ratio of 0.47 were investigated using AC impedance spectroscopy [11, 19] in argon gas from 1 573 to 1 773 K, and the effect of FeO and NiO on the electrical conductivity in the low basicity slags was discussed as a fundamental study on extraction of valuable metals from the nonferrous metallurgical slags.
2 Experimental
Composition of experimental slags is listed in Table 1. Analytical reagent grades of MgO, Al2O3, SiO2, NiO, CaCO3 and Fe2CO4·2H2O were used as raw materials to synthesize the experimental slags directly, in which CaCO3 and Fe2CO4·2H2O were used as CaO and FeO respectively for accurate weighing in experimental process. The testing temperatures were 1 573, 1 623, 1 673, 1 723 and 1 773 K, respectively.
Table 1 Chemical composition of molten slags
A scheme of experimental apparatus is shown in Fig. 1. Two parallel platinum pieces (length of 40 mm, width of 10 mm, thickness of 0.5 mm) used as electrodes were connected respectively with two platinum wires (d= 1 mm) to an electrochemical analyzer (CHI660). The platinum wires and a part of the platinum pieces were fixed into the thin corundum tubes in which some high temperature cements were used to fill for preventing the vibration and bend of the electrodes. 90 g slags with the chemical composition shown in Table 1 were set into a corundum crucible (40 mm O.D., 35 mm I.D., 100 mm H) and then placed into an electric furnace. The furnace was heated to the testing temperature (±2 K), and then maintained for 30 min to ensure the slag melted completely. The electrodes were subsequently immersed into molten slags. High pure argon as an inert gas was continuously flushing into the furnace with a flowing rate of 1 000 mL/min to prevent oxidation of the slag in experimental process. The cell constant (κ=lS, where l is a distance between two electrodes, 8 mm; S is an area of the electrodes immersed in molten slags, 246 mm2) measured using 0.1 mol/L KCl standard solution at 292 K, was (32.5±0.1) m-1.
Fig. 1 Schematic diagram of experimental apparatus
The equivalent circuit for the cell is shown in Fig. 2. Total impedance (Z) can be divided into three parts: the first part impedance (Z1) contains the apparent resistance (Rb) with the resistance of the electrodes and lead wires, the second part impedance (Z2) contains electron-charge transfer resistance (Rct) at electrode interfaces, double layer capacitance (Cdl) and Warburg impedance (Zw), and the last part impedance (Z3) contains inductance (Le) of the lead wires.
Fig. 2 Equivalent circuit for cell
The impedances of the apparent resistance, the electron-charge transfer resistance, the Warburg impedance, double layer capacitance, and the inductance of lead wires are as follows respectively:
(1)
(2)
(3)
where k is constant.
(4)
(5)
The first part impedance (Z1), the second part impedance (Z2) and the last part impedance (Z3) are as follows:
(6)
(7)
(8)
Total impedance can be expressed according to the equivalent circuit as shown in Eq. (6).
(9)
Eq. (9) is replaced by Eqs. (1)-(8), which obtains
(10)
where
；
；
；
.
And then Z′ and Z″ in Eq. (6) can be induced as real part and imaginary part as follows:
(11)
(12)
Therefore, Z′ and Z″ measured by AC impedance spectroscopy were fitted to calculate the apparent resistance (Rb) according to Eq. (11) and Eq. (12) using nonlinear least-squares. The resistance of lead wires was measured at different temperatures by AC impedance spectroscopy shown in Table 2.
Table 2 Resistances of electrodes and lead wires at different temperatures
The resistance of molten slags (R) can be given by
(13)
And then the electrical conductivity (σ) of molten slags is calculated as follows:
(14)
3 Results and discussion
Figure 3 shows AC impedance spectra of base slag from 1 573 K to 1 773 K, in which points and lines were obtained from the experimental data and fitting values by Eq. (11) and Eq. (12) respectively. It is noticeable that, in high frequency region, AC impedance spectra are in the forth quadrant, which indicates Le played a major role. Comparatively, Rct, Cdl and Zw played the major role in low frequency region. When AC impedance spectra intersect with the real axis (Z″=0), Z′ equated to the impedance of the apparent resistance (Rb). Therefore, it can be considered that the resistance of molten slags decreased with the increase of temperature because the resistance of the electrodes and lead wires has a minor change from 1.19 Ω to 1.26 Ω at different temperatures.
Fig. 3 AC impedance spectra of base slag at different temperatures
Figure 4 shows the AC impedance spectra of FeO-CaO-MgO-SiO4-Al2O3 slags from 1 573 K to 1 773 K. The apparent resistance (Rb) was decreased with the increase of FeO content. It can be considered that the three-dimensional network structure of silicate was destroyed with increasing FeO content, thus many ions with free migration were produced in molten slags.
Figure 5 shows the AC impedance spectra of NiO-CaO-MgO-SiO4-Al2O3 slags from 1 573 K to 1 773 K. The apparent resistance decreased with the increase of NiO content, which has a similar trend in the case of adding FeO.
The electrical conductivities of molten slags was calculated by Eq. (13) and Eq. (14), and were shown in Table 3. The electrical conductivity increased from 1.4 S/m to 14.4 S/m with the increases of the temperature and MO content, which is close to that in previous measurements for similar slag.
Figure 6 shows the plot of electrical conductivity of molten slags as a function of MO content. The increase of electrical conductivity was promoted with the increase
of MO content. The electrical conductivity of FeO- containing slags was close to that of NiO-containing slags when the content was less than 8%; however, it was obviously larger than that of NiO-containing slags when the content was 12%. The electrode reactions at standard state are
(15)
(16)
where φθ is standard electrode potentials, in which the standard potential of Fe2+ formed from Fe3+ is lower than that of Ni2+ formed from Ni3+. So Fe2+ is easier to lose an electron than Ni2+, which indicates that Fe2+ is more beneficial to increase the electronic conductivity in molten slags. Therefore, the electrical conductivity of FeO-containing slags was larger than that of NiO- containing slags when MO content was enough high, e.g. 12%.
Fig. 4 AC impedance spectra of FeO-CaO-MgO- SiO2-Al2O3 slags at different temperatures
Fig. 5 AC impedance spectra of NiO-CaO-MgO- SiO2-Al2O3 slags at different temperatures
Table 3 Electrical conductivities measured and comparison with previous data
Fig. 6 Electrical conductivity as function of MO content
Fig. 7 Arrhenius plot of electrical conductivity: (a) FeO-CaO- MgO-SiO2-Al2O3 slags; (b) NiO-CaO-MgO- SiO2-Al2O3 slags
Figure 7 shows a plot of logarithm of the electrical conductivity as a function of reciprocal of temperature, where E as the activation energy of the electrical conductivity was obtained according to an Arrhenius-type relation shown in Eq. (17),
(17)
where A and R is the pre-exponential factor and the gas constant, respectively.
The activation energy of the electrical conductivity decreased with the increase of MO content, which has a good agreement with the results from previous researchers shown in Fig. 8. The activation energy was higher than that of LU et al [11] because the basicity of molten slags in present work was lower, and it could be also explained by the experimental results of SARKAR [20] that the activation energy of the electrical conductivity decreased with the increase of the basicities. Moreover, the activation energy of FeO-containing slags was lower than that of NiO-containing slags, and the activation energy of FeO-containing slags decreased larger than that of NiO-containing slags with the increase of the content.
Fig. 8 Activation energy as function of MO content
4 Conclusions
1) The electrical conductivities of MO(MO=FeO, NiO)-CaO-MgO-Al2O3-SiO2 slags with (CaO+MgO)/ (SiO2+Al2O3) mass ratio of 0.47 and MO content of 0-12%, were measured by AC impedance spectroscopy from 1 573 K to 1 773 K.
2) The Z′ and Z″ calculated from equivalent circuit are well consistent with the experimental results obtained by AC impedance spectra, and the electrical conductivities of molten slags increased from 1.4 S/m to 14.4 S/m with the increases of temperature and MO content.
3) The increase of the electrical conductivity was promoted with the increase of MO content in the low basicity slags, but the electrical conductivity of FeO-containing slags was close to that of NiO-containing slags when the content was less than 8%; it was obviously larger than that of NiO-containing slags when the content was 12%.
4) Activation energies of the electrical conductivity decreased with the increase of MO content, and the activation energy of FeO-containing slags decreased larger than that of NiO-containing slags with the further increase of MO content.
References
[1] BRITTEN S C, PAL U B. Solid-state amperometric sensor for the in-situ monitoring of slag composition and transport properties [J]. Metallurgical and Materials Transactions B, 2000, 31: 733-752.
[2] GAO Yun-ming, GUO Xing-min, CHOU Kuo-chih. Unpolluted short circuit electrochemical reduction analysis for molten oxide slags [J]. The Chinese Journal of Nonferrous Metals, 2006, 16(3): 530-535. (in Chinese)
[3] SUN Chang-yu, GUO Xing-min. Continual preparation of ferronickel by no-contacting smelting reduction method [J]. Journal of University of Science and Technology Beijing, 2010, 32(7): 900-904. (in Chinese)
[4] FISCHER V W A, ENDE H V. Das spezifische elektrische leitvermogen von eisenoxydulhaltigen schlacken [J]. Archiv fur das Eisenhuttenwesen, 1951, 22: 417-423. (in German)
[5] ADACHI A, OGINO K. Electrical conductivity of oxidized slags [J]. Technology Reports of the Osaka University, 1957, 7(244): 121-126.
[6] NARITA K, ONOYE T, ISHII T, UEMURA K. The electrical conductivity of CaO-SiO2-FetO slag [J]. The Journal of the Iron and Steel Institute of Japan, 1975, 61(14): 2943-2951.
[7] HOSTER T, ESSEN J P. The electric conductivity of FeO-containing CaO-Al2O3-SiO2 slags with basicities ≤1.5 at 1450 to 1650 °C [J]. Archiv Eisenhuttenwes, 1983, 54: 389-394.
[8] BARATI M, COLEY K S. Electrical and electronic conductivity of CaO-SiO2-FeOx slags at various oxygen potentials: Part I. Experimental results [J]. Metallurgical and Materials Transactions B, 2006, 37: 41-49.
[9] DAI Xi, ZHANG Chun-fu. Electrical conductivity measurement of FeO-MgO-CaO-SiO2 slag [J]. Nonferrous Metallurgy: Smelting Part, 2005(4): 2-4. (in Chinese)
[10] BOBOK L, BODNAR L, SCHMIEDL J. Specific electric conductivity of Fe-O-SiO2-X slag systems [J]. Hutnicke Listy, 1982, 37(6): 419-424.
[11] LU Xiong-gang, LI Fu-shen, LI Li-fen, ZHOU Guo-zhi. Application of AC impedance for measuring resistance of slag [J]. The Chinese Journal of Nonferrous Metals, 2000, 10(3): 437-439. (in Chinese)
[12] SHIN S N, LYAMKIN S A, GULYAEVA R I, CHUMAREV V M. Electrical conductivity of melts FeOx-Al2O3-CaO-SiO2 system [J]. Rasplavy, 1998(5): 20-24.
[13] KAWAHARA M, MORINAGA K J, YANAGASE T. Behavior of MgO and NiO in molten slags [J]. Canadian Metallurgical Quarterly, 1983, 22(2): 143-147.
[14] GUO Xing-min, GAO Yun-ming, ZHANG Yi, ZHOU Guo-zhi, HU Xiao-jun, LI Fu-xin. Studies on slag structure and the reducibility for diluted slag of Jinchuan’s flash smelting furnace [J]. Metallurgy Research, 2002: 346-351. (in Chinese)
[15] CAO Zhan-min, SUN Gen-sheng, RICHTER K, QIAO Zhi-yu. Microstructure and metal distribution in Jinchuan nickel smelting slag [J]. Journal of University of Science and Technology Beijing, 2001, 23(4): 316-319. (in Chinese)
[16] HUNDERMARK R J, JAHANSHAHI S, SUN S. Electrical conductivity of melter type slags [C]// LORENZEN L, BRADSHOW D J. 22nd International Mineral Processing Congress. Cape Town, South Africa, 2003: 1370-1377.
[17] FONTANA A, SEGERS L, TWITE K, WINAND R. Electrical conductivity of ferrous silicate melts from slag cleaning operations [C]//TMS-AIME Paper Selection A. 1984: 84.
[18] Slag Atlas [M]. 2nd ed. Verein Deutscher Eisenhuttenleute, 1995.
[19] WANG S L, LI G Q, LOU T P, SUI Z T. The conductivity and the crystallization of perovskite (CaTiO3) from Ti-bearing blast furnace slag studied by A.C. impedance method [J]. ISIJ International, 1999, 39(11): 1116-1119.
[20] SARKAR S B. Electrical conductivity of molten high-alumina blast furnace slags [J]. ISIJ International, 1989, 29(4): 348-351.
含MO(MO=FeO,NiO)的低碱度CaO-MgO-Al2O3-SiO2熔渣电导率
孙长余，郭兴敏
北京科技大学 冶金与生态工程学院，北京 100083
摘 要：作为有色冶金渣中有价金属回收基础，利用电化学交流阻抗谱法，测定低碱度MO(MO=FeO,NiO)- CaO- MgO-Al2O3-SiO2五元熔渣体系的电导率。结果表明：随着熔渣体系温度的升高和MO浓度的增大，熔渣电导率增大。在1 573~1 773 K下, (CaO+MgO)与(SiO2+Al2O3)质量比为0.47，当MO浓度小于12%时，熔渣电导率为1.4~14.4 S/m。随着熔渣中MO浓度的增大，熔渣电导率增大的幅度增加。当熔渣中FeO和NiO浓度小于8%时，两种熔渣的电导率相差不大；当浓度达到12%时，含FeO的熔渣电导率明显大于含NiO的熔渣电导率。随着MO浓度的增加，电导活化能降低。
关键词：FeO；NiO；熔渣；电导率；交流阻抗
(Edited by YANG Hua)
Foundation item: Project (50574011) supported by the National Natural Science Foundation of China
Corresponding author: GUO Xing-min; Tel: +86-10-62334957; E-mail: guoxm@ustb.edu.cn
DOI: 10.1016/S1003-6326(11)60909-6