Preparation Technology and Performances of Zn-Cr Coating on Sintered NdFeB Permanent Magnet

来源期刊:JOURNAL OF RARE EARTHS2006年第2期

论文作者:Chen Ling Yu Shengxue

Key words:sintered NdFeB permanent magnet; Zn-Cr coating; magnet property; anticorrosion property; rare earths;

Abstract: Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established.The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB.Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured.The micro-morphology and composition of Zn-Cr coating were analyzed through SEM, XPS, EDS and XRD.The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated.It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection.The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.

详情信息展示

Preparation Technology and Performances of Zn-Cr Coating on Sintered NdFeB Permanent Magnet

Chen Ling1,Yu Shengxue1

(1.Department of Applied Chemistry, Yanshan University, Qinhuangdao 066004, China)

Abstract:Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established.The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB.Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured.The micro-morphology and composition of Zn-Cr coating were analyzed through SEM, XPS, EDS and XRD.The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated.It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection.The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.

Key words:sintered NdFeB permanent magnet; Zn-Cr coating; magnet property; anticorrosion property; rare earths;

【全文内容正在添加中】

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号