Microstructure evolution of nanostructured ferritic alloy with and without Cr3C2c oated SiC at high temperatures
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2020年第8期
论文作者：Kaustubh Bawane Kathy Lu
文章页码：126 - 134
摘 要：This work focuses on fundamental understanding of microstructure evolution of nanostructured ferritic alloy（NFA） and 25 vol.% Cr3C2 coated Si C（Cr3C2@Si C）-NFA composite during spark plasma sintering at950°C and the following thermal treatment at 1000°C. A unique bi-phase microstructure with distinct Cr-rich and Si-rich phases has been observed for the 25 vol.% Cr3C2@Si C-NFA composite, while for the NFA sample, the traditional large grain microstructure remains. Grain sizes are significantly smaller for the25 vol.% Cr3C2@Si C-NFA composite compared to those for the pure NFA, which can be attributed to the presence of grain boundary phases in the composite sample. During the thermal treatment, microstructure features can be directly correlated with the dissolution kinetics and phase diagrams calculated using Thermo-Calc/DICTRA/PRISMA?.
Kaustubh Bawane，Kathy Lu
Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University
摘 要：This work focuses on fundamental understanding of microstructure evolution of nanostructured ferritic alloy（NFA） and 25 vol.% Cr3C2 coated Si C（Cr3C2@Si C）-NFA composite during spark plasma sintering at950°C and the following thermal treatment at 1000°C. A unique bi-phase microstructure with distinct Cr-rich and Si-rich phases has been observed for the 25 vol.% Cr3C2@Si C-NFA composite, while for the NFA sample, the traditional large grain microstructure remains. Grain sizes are significantly smaller for the25 vol.% Cr3C2@Si C-NFA composite compared to those for the pure NFA, which can be attributed to the presence of grain boundary phases in the composite sample. During the thermal treatment, microstructure features can be directly correlated with the dissolution kinetics and phase diagrams calculated using Thermo-Calc/DICTRA/PRISMA?.
关键词：