Preparation and tensile properties of Al2O3/Ni-Co nanocomposites
来源期刊：中国有色金属学报(英文版)2011年第z2期
论文作者：WANG Guo-feng JIANG Shao-song LU Zhen ZHANG Kai-feng
文章页码：374 - 379
Key words：additives; composites; mechanical properties; pulse current electrodeposition
Abstract: Al2O3/Ni-Co composites with different additives and Al2O3 particles were fabricated by pulse current electrodeposition. The effects of different additives and Al2O3 particles on the surface smoothness, micro-hardness and plastic deformation at room temperature and high temperature were compared. Scanning electron microscopy was employed to examine the microstructures of the as-deposited and deformed samples. The hardness, fracture strength at room temperature and elongation at superplastic temperature of the material reach HV469, 1 150 MPa and 632%, respectively, when the saccharin was used as additive.
WANG Guo-feng, JIANG Shao-song, LU Zhen, ZHANG Kai-feng
(School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
Abstract:Al2O3/Ni-Co composites with different additives and Al2O3 particles were fabricated by pulse current electrodeposition. The effects of different additives and Al2O3 particles on the surface smoothness, micro-hardness and plastic deformation at room temperature and high temperature were compared. Scanning electron microscopy was employed to examine the microstructures of the as-deposited and deformed samples. The hardness, fracture strength at room temperature and elongation at superplastic temperature of the material reach HV469, 1 150 MPa and 632%, respectively, when the saccharin was used as additive.
Key words:additives; composites; mechanical properties; pulse current electrodeposition