Nonionic Polymerizable Emulsifier in High-Solids-Content Acrylate Emulsion Polymerization
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2012年第5期
论文作者：鲁德平 管蓉
文章页码：924 - 930
摘 要：Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.
鲁德平，管蓉
Ministry of Education,Key Laboratory for the Synthesis and Application of Organic Functional Molecules,College of Chemistry and Chemical Engineering,Hubei University
摘 要：Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.
关键词：