Preparation and Magnetostriction of Tb0.22Dy0.48Ho0.35Fe2 Alloys
来源期刊：Journal of Rare Earths2007年第S2期
论文作者：江民红
文章页码：198 - 201
摘 要：Tb0.22Dy0.48Ho0.35Fe2 quaternary alloys are prepared by melting-top casting-annealing process. X-ray diffraction reveals that the alloy is single phase polycrystalline alloy with MgCu2 type cubic Laves phase structure, and （511） preferred orientation occurs in its. The magnetostriction measurements are carried out at room temperature using standard strain gauge technique in magnetic fields up to 400 kA·m-1. The results show that when the magnetic field, H, is 90 kA·m-1, the magnetostriction, λ, of Tb0.22Dy0.48Ho0.35Fe2 quaternary alloys is 260×10-6, and when the H is 210 kA·m-1, the λ is 438×10-6. When the H is 400 kA·m-1, the λ is up to the saturation value, 538×10-6. As compared with TbDyFe ternary alloys, the λ of the quaternary alloy is significantly higher when the H is less than or equal to 210 kA·m-1. When the H is 120 kA·m-1, the λ of the alloy is 333×10-6, 70×10-6 more than the ternary alloy. Research results and mechanism are discussed.
江民红
摘 要：Tb0.22Dy0.48Ho0.35Fe2 quaternary alloys are prepared by melting-top casting-annealing process. X-ray diffraction reveals that the alloy is single phase polycrystalline alloy with MgCu2 type cubic Laves phase structure, and （511） preferred orientation occurs in its. The magnetostriction measurements are carried out at room temperature using standard strain gauge technique in magnetic fields up to 400 kA·m-1. The results show that when the magnetic field, H, is 90 kA·m-1, the magnetostriction, λ, of Tb0.22Dy0.48Ho0.35Fe2 quaternary alloys is 260×10-6, and when the H is 210 kA·m-1, the λ is 438×10-6. When the H is 400 kA·m-1, the λ is up to the saturation value, 538×10-6. As compared with TbDyFe ternary alloys, the λ of the quaternary alloy is significantly higher when the H is less than or equal to 210 kA·m-1. When the H is 120 kA·m-1, the λ of the alloy is 333×10-6, 70×10-6 more than the ternary alloy. Research results and mechanism are discussed.
关键词：