Analysis on Interface Characteristics of FeNi_p/PP Nanocomposites
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2019年第6期
论文作者:钟麒 朱正吼 BAI Ruru CHEN Jie
文章页码:1248 - 1253
摘 要:The FeNip/PP nanocomposites were successfully prepared by the two-step blending method and the permeable layer interface with thickness of 2 to 10 nm was formed on the surface of nanopowders. The interface is composed of the lattice and molecular chain, in which the polypropylene molecular chain enters the lattice defects and forms a cross-linked structure. The interface causes the FeNi nanopowders to be well compatible with the polypropylene matrix and uniformly dispersed in the matrix, and significantly improves the mechanical properties of composites. The tensile strength of 2 wt% FeNip/PP composites reached 38 MPa, 23% higher than that of pure PP resin. The shielding performance of 20 wt% FeNip/PP composites reached 9.8 dB in the frequency range of 1-100 MHz.
钟麒,朱正吼,BAI Ruru,CHEN Jie
College of Material Science and Engineering, Nanchang University
摘 要:The FeNip/PP nanocomposites were successfully prepared by the two-step blending method and the permeable layer interface with thickness of 2 to 10 nm was formed on the surface of nanopowders. The interface is composed of the lattice and molecular chain, in which the polypropylene molecular chain enters the lattice defects and forms a cross-linked structure. The interface causes the FeNi nanopowders to be well compatible with the polypropylene matrix and uniformly dispersed in the matrix, and significantly improves the mechanical properties of composites. The tensile strength of 2 wt% FeNip/PP composites reached 38 MPa, 23% higher than that of pure PP resin. The shielding performance of 20 wt% FeNip/PP composites reached 9.8 dB in the frequency range of 1-100 MHz.
关键词: