Effect of addition of Al-Si eutectic alloy on microstructure and mechanical properties of Mg-12wt%Li alloy
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2018年第9期
论文作者:Zilong Zhao Xuegang Xing Jinyu Ma Liping Bian Wei Liang Yide Wang
文章页码:1564 - 1569
摘 要:Mg-12 Li, Mg-12 Li-3(Al-Si), Mg-12 Li-7(Al-Si) and Mg-12 Li-9(Al-Si) alloys(all in wt%) were fabricated by high frequency vacuum induction melting in a water cooled copper crucible. After subsequently hotrolling and annealing, their microstructure and mechanical properties were investigated. Experimental results show that mechanical properties of Mg-12 Li alloy were significantly improved by the addition of Al-Si eutectic alloy. Mg-12 Li-7(Al-Si) alloy shows the highest strength of 196 MPa of the investigated alloys, which is about 1.8 times of the strength of Mg-12 Li alloy, and maintains high elongation of 27%.The improved mechanical property with addition of Al and Si in the eutectic proportion into Mg-12 Li alloy was attributed to the solution strengthening effect of A1 and precipitation hardening effect from AlLi and Mg2 Si precipitates.
Zilong Zhao1,Xuegang Xing2,Jinyu Ma1,Liping Bian1,3,Wei Liang1,3,Yide Wang3
1. College of Materials Science and Engineering, Taiyuan University of Technology2. Institute of Applied Mechanics and Biomedical Engineering, Taiyuan University of Technology3. Shanxi Key Laboratory of Advanced Magnesium-Based Materials
摘 要:Mg-12 Li, Mg-12 Li-3(Al-Si), Mg-12 Li-7(Al-Si) and Mg-12 Li-9(Al-Si) alloys(all in wt%) were fabricated by high frequency vacuum induction melting in a water cooled copper crucible. After subsequently hotrolling and annealing, their microstructure and mechanical properties were investigated. Experimental results show that mechanical properties of Mg-12 Li alloy were significantly improved by the addition of Al-Si eutectic alloy. Mg-12 Li-7(Al-Si) alloy shows the highest strength of 196 MPa of the investigated alloys, which is about 1.8 times of the strength of Mg-12 Li alloy, and maintains high elongation of 27%.The improved mechanical property with addition of Al and Si in the eutectic proportion into Mg-12 Li alloy was attributed to the solution strengthening effect of A1 and precipitation hardening effect from AlLi and Mg2 Si precipitates.