Preparation of rare-earth-modified medical stone powders and their application as conductive fillers

来源期刊:International Journal of Minerals Metallurgy and Materials2019年第2期

论文作者:Li-ying Qi Su-e Hao Tian-cheng Sun

文章页码:260 - 266

摘    要:Traditional metal conductive fillers are expensive and prone to oxidation. Thus, the development of new conductive powders as fillers is urgently needed. A novel gaseous penetration technology was adopted to prepare La-doped medical stone powders(La-MSPs), which are inexpensive mesoporous materials, as a new kind of conductive filler material. The prepared La-MSPs attained a resistivity of 450 ?·m and were used as a filler to prepare conductive coatings with epoxy resin as the resin matrix. The influence of the La-MSPs dosage on the resistance and hardness of the coatings was also determined. The resistance and the hardness both decreased with increasing filler dosage. Finally, the optimum recipe of the conductive coatings with the most suitable fillers dosage(55 wt%) was obtained. The hardness and resistance of the coatings with 55 wt% La-MSPs were HV 4 and 5.5 × 107 ?, respectively.

详情信息展示

Preparation of rare-earth-modified medical stone powders and their application as conductive fillers

Li-ying Qi,Su-e Hao,Tian-cheng Sun

School of Chemistry and Chemical Engineering, Harbin Institute of Technology

摘 要:Traditional metal conductive fillers are expensive and prone to oxidation. Thus, the development of new conductive powders as fillers is urgently needed. A novel gaseous penetration technology was adopted to prepare La-doped medical stone powders(La-MSPs), which are inexpensive mesoporous materials, as a new kind of conductive filler material. The prepared La-MSPs attained a resistivity of 450 ?·m and were used as a filler to prepare conductive coatings with epoxy resin as the resin matrix. The influence of the La-MSPs dosage on the resistance and hardness of the coatings was also determined. The resistance and the hardness both decreased with increasing filler dosage. Finally, the optimum recipe of the conductive coatings with the most suitable fillers dosage(55 wt%) was obtained. The hardness and resistance of the coatings with 55 wt% La-MSPs were HV 4 and 5.5 × 107 ?, respectively.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号