Effects of Fe Modified Na2WO4 Additive on the Hydrogen Storage Properties of MgH2
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2019年第5期
论文作者：王家盛 张伟 LI Bo SHEN Na HUO Quan
文章页码：1030 - 1036
摘 要：A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen storage properties of MgH2 together with the corresponding mechanism were investigated. At 423 K, within the first 200 seconds, the hydrogen absorption amount of MgH2+20 wt% Fe2O3/Na2WO4 was almost 5 times that of pure MgH2. And at 573 K, its total hydrogen desorption amount was 7 times that for pure MgH2. Meanwhile, its onset dehydrogenation temperature was 110 K lower than that of pure MgH2. It was worth noting that the MgH2+20 wt% Fe/Na2WO4 presented the lower dehydrogenation reaction activation energy（Ea） of 35.9 kJ·mol-1 compared to that of pure MgH2. The active MgWO4, Mg2 FeH6 and MgO formed during the milling process were responsible for the improvement of the hydrogen storage properties for MgH2.
王家盛1，张伟2，LI Bo1，SHEN Na2，HUO Quan2
1. Department of Environmental Engineering, North China Institute of Science and Technology2. Hebei Key Laboratory of Applied Chemistry, School of Environmental and Chemical Engineering, Yanshan University
摘 要：A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen storage properties of MgH2 together with the corresponding mechanism were investigated. At 423 K, within the first 200 seconds, the hydrogen absorption amount of MgH2+20 wt% Fe2O3/Na2WO4 was almost 5 times that of pure MgH2. And at 573 K, its total hydrogen desorption amount was 7 times that for pure MgH2. Meanwhile, its onset dehydrogenation temperature was 110 K lower than that of pure MgH2. It was worth noting that the MgH2+20 wt% Fe/Na2WO4 presented the lower dehydrogenation reaction activation energy（Ea） of 35.9 kJ·mol-1 compared to that of pure MgH2. The active MgWO4, Mg2 FeH6 and MgO formed during the milling process were responsible for the improvement of the hydrogen storage properties for MgH2.