用电子束辐照法在模具表面制备陶瓷/金属复合层（英文）
来源期刊：材料与冶金学报2015年第2期
论文作者：赤尾尚洋 樱井雄基 音田哲彦 上原和武 陈中春
文章页码：152 - 158
摘 要：Surface modifications,which result in formation of a hard layer such as CrN,TiN,TiCN etc. on tool surfaces,have been widely utilized in machining tools. How ever,the hard layer has clear interface with the matrix,thereby the delamination between the hard layer and matrix often occurs because of a mismatch of the thermal expansion coefficients. A composite layer with complicated interfaces between hard material and matrix is desired to avoid such a delamination due to a complicated interface existed between workpiece and coating materials. In this study,the formation of ceramic- metal composite layers on the surfaces of die steels by an electron beam（ EB） irradiation technique has been investigated. When WC- Co powder was embrocated onto the substrate surfaces,a composite layer of WC- Co and matrix was formed through solidification after the irradiation-induced melting. The composite layer shows a marble- like texture with WC- rich regions. The hardness of the layer reaches up to 1000 HV. For other ceramic pow ders such as TiN and SiC,only small amount of particles has been incorporated into the composite layer,resulting in a relatively low hardness enhancement after the EB irradiation.
赤尾尚洋1，樱井雄基1，音田哲彦1，上原和武2，陈中春1
1. Department of Mechanical and Aerospace Engineering,Graduate School of Engineering,Tottori University2. Next Generation Advanced Medical Promotion Center,Tottori University Hospital
摘 要：Surface modifications,which result in formation of a hard layer such as CrN,TiN,TiCN etc. on tool surfaces,have been widely utilized in machining tools. How ever,the hard layer has clear interface with the matrix,thereby the delamination between the hard layer and matrix often occurs because of a mismatch of the thermal expansion coefficients. A composite layer with complicated interfaces between hard material and matrix is desired to avoid such a delamination due to a complicated interface existed between workpiece and coating materials. In this study,the formation of ceramic- metal composite layers on the surfaces of die steels by an electron beam（ EB） irradiation technique has been investigated. When WC- Co powder was embrocated onto the substrate surfaces,a composite layer of WC- Co and matrix was formed through solidification after the irradiation-induced melting. The composite layer shows a marble- like texture with WC- rich regions. The hardness of the layer reaches up to 1000 HV. For other ceramic pow ders such as TiN and SiC,only small amount of particles has been incorporated into the composite layer,resulting in a relatively low hardness enhancement after the EB irradiation.
关键词：