7475铝合金ECAP的晶粒细化极限

来源期刊:中国有色金属学报2004年第5期

论文作者:张郑 王经涛 赵西成

文章页码:741 - 745

关键词:7475铝合金;等径弯曲通道变形; 晶粒细化极限; 沉淀相粒子

Key words:aluminum 7475 alloy; equal-channel angular pressing; grain refinement limit; precipitate

摘    要:将等径弯曲通道变形应用于7475铝合金, 等效真应变达12。 对7475铝合金在不同温度下ECAP变形后显微组织特征和晶粒细化极限进行了研究。 结果表明: 变形温度从273K到773K, 7475铝合金的晶粒细化极限为0.29 ~1.90μm,且极限晶粒尺寸的倒数与变形温度的倒数成正比关系。 在较高温度下, 组织中产生大量的沉淀相粒子能有效钉扎晶界, 阻碍晶粒长大, 使合金具有较好的组织热稳定性。

Abstract: Equal-channel angular pressing was conducted on a 7475 aluminum alloy at temperature from room temperature to 773K up to an equivalent true strain of 12. The grain refinement limit was dependent upon the precise pressing temperature, and the grain was refined to within the range from 0.29 to 1.9μm by ECAP at these different temperatures. At higher temperature, it is apparent that these precipitates may be important in pinning the grain boundaries and thus increasing the thermal stability of the sub-micrometer-grained structure.



详情信息展示

 

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 主办 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:新出网证(湘)字005号   湘ICP备09001153号