Performance of RAP in the System of Cold Inplace Recycling of Asphalt Pavement
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第6期
论文作者：马保国
文章页码：1211 - 1214
摘 要：The property of reclaimed asphalt pavement（RAP） mixture will be affected mainly by composition of old asphalt/soil and cement content in CIR system. We studied the relationship between A/S and cementitious materials. It showed that if there was no soil in RAP, the unconfined compressive strength was only from 0.18 MPa to 1.07 MPa even if adding cement was from 2% to 6%, and RAP samples collapsed during conserving in water. The optimum water content rose from 6.5% to 11% with the declining of A/S from S=0 to A/S=1/5. Five RAP samples all got the maximum compressive strength when A/S=5/5, and the maximum compressive strength of the samples adding 6% cement was 3.17 MPa. It showed that the capacity of RAP was not only affected by A/S, but also by the content of cement. The dynamic modulus of RAP will increase with the rise of loading frequency and decrease with the temperature rising. SEM test showed that C-S-H interlacing formed the netted structure, and it enwrapped the aggregate and improved the strength of RAP.
马保国
Key Laboratory for Silicate Materials Science and Engineering of Ministry of Education,Wuhan University of Technology
摘 要：The property of reclaimed asphalt pavement（RAP） mixture will be affected mainly by composition of old asphalt/soil and cement content in CIR system. We studied the relationship between A/S and cementitious materials. It showed that if there was no soil in RAP, the unconfined compressive strength was only from 0.18 MPa to 1.07 MPa even if adding cement was from 2% to 6%, and RAP samples collapsed during conserving in water. The optimum water content rose from 6.5% to 11% with the declining of A/S from S=0 to A/S=1/5. Five RAP samples all got the maximum compressive strength when A/S=5/5, and the maximum compressive strength of the samples adding 6% cement was 3.17 MPa. It showed that the capacity of RAP was not only affected by A/S, but also by the content of cement. The dynamic modulus of RAP will increase with the rise of loading frequency and decrease with the temperature rising. SEM test showed that C-S-H interlacing formed the netted structure, and it enwrapped the aggregate and improved the strength of RAP.
关键词：