INTERFACIAL REACTION BEHAVIOUR AND JOINT STRENGTH OF TiCp/Si3N4 COMPOSITE BONDED WITH Al FOIL
来源期刊：中国有色金属学报(英文版)1999年第1期
论文作者：Zhou Fei Li Zhizhang Luo Qifu
文章页码：115 - 120
Key words：Si3N4 ceramic composite; Al foil; interfacial reaction; metal joint; ceramic joint
Abstract: The joints of Si3N4composite bonded with Al foil were treated by metal joint becoming ceramics. Reaction behavior of the interface between Si3N4and Al in joining of TiCp/Si3N4composite with Al foil was studied by means of SEM, EPMA, XRD and AES. The results show that Si, N and O diffuse from the TiCp/Si3N4composite into Al liquid phase zone to produce AlN, Al2O3·SiO2at 1273K, while at 1173K, only alumina is detected at interface. The thermodynamic and thermal stress analyses at the interface show that the interfacial reactions of interface are influenced not only by bonding temperature and the oxide formed at the faying surface before bonding, but also by the atmosphere of the furnace containing graphite heating ele- ments. The effect of bonding temperature on joint strength depends on the effect of joining temperature on reaction products at the interface. The room and high temperature strengths are enhanced after metal joints have become ceramic.