Isothermal section of Nd-Zr-Si ternary system at 773 K
来源期刊：Journal of Rare Earths2012年第1期
论文作者：何建贤 何维 姚祥 曾令民
文章页码：79 - 83
摘 要：Phase diagram is an important basis for materials research and materials application.The phase relations of the Nd-Zr-Si ternary system at 773 K were investigated by X-ray powder diffraction analysis,metallographic analysis and scanning electron microscopy with en-ergy dispersive analysis.The isothermal section of the phase diagram of the Nd-Zr-Si ternary system at 773 K was determined.The isother-mal section of the system consisted of 13 single-phase regions,23 two-phase regions and 11 three-phase regions.The homogeneity range of α-NdSix was from 63 at.% to 66 at.% Si（with x=1.70-1.94）.The maximum solid solubilities of Nd in Zr-Si binary compounds and Zr in the Nd-Si binary compounds were observed less than 1 at.% at 773 K.
何建贤，何维，姚祥，曾令民
Key Laboratory of Nonferrous Metal Materials and New Processing Technology of Ministry of Education,College of Materials Science and Engineering,Guangxi Uni-versity
摘 要：Phase diagram is an important basis for materials research and materials application.The phase relations of the Nd-Zr-Si ternary system at 773 K were investigated by X-ray powder diffraction analysis,metallographic analysis and scanning electron microscopy with en-ergy dispersive analysis.The isothermal section of the phase diagram of the Nd-Zr-Si ternary system at 773 K was determined.The isother-mal section of the system consisted of 13 single-phase regions,23 two-phase regions and 11 three-phase regions.The homogeneity range of α-NdSix was from 63 at.% to 66 at.% Si（with x=1.70-1.94）.The maximum solid solubilities of Nd in Zr-Si binary compounds and Zr in the Nd-Si binary compounds were observed less than 1 at.% at 773 K.
关键词：