Abrasive wear characteristics and mechanisms of Al2O3/PA1010 composite coatings
来源期刊:Rare Metals2004年第1期
论文作者:JIA Xian, and LING Xiaomei) Department of Science and Technology, University of Science and Technology Beijing, Beijing , China) Department of Analytical Chemistry, School of Pharmaceutical Science, Peking University, Beijing , China
文章页码:59 - 63
摘 要:<正> The abrasive wear characteristics of Al2O3/PA1010 composite coatings on the surface of quenched and low-temperature temper steel 45 were tested on the template abrasive wear testing machine and the same uncoated steel 45 was used as a reference material. Experimental results showed that the abrasive wear resistance of Al2O3/PA1010 composite coatings has a good linear relationship with the volume fraction of Al2O3 particles in Al2O3/PA1010 composite coatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, the size of Al2O3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance of Al2O3/PA1010 composite coatings. By treating the surface of Al2O3 particles with a suitable bonding agent, the distribution of Al2O3 particles in matrix PA1010 is more homogeneous and the bonding state between Al2O3 particles and matrix PA1010 is better. Therefore, the Al2O3 particles in Al2O3/PA1010 composite coatings make the Al2O3/PA1010 composite coatings have bet
摘要:<正> The abrasive wear characteristics of Al2O3/PA1010 composite coatings on the surface of quenched and low-temperature temper steel 45 were tested on the template abrasive wear testing machine and the same uncoated steel 45 was used as a reference material. Experimental results showed that the abrasive wear resistance of Al2O3/PA1010 composite coatings has a good linear relationship with the volume fraction of Al2O3 particles in Al2O3/PA1010 composite coatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, the size of Al2O3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance of Al2O3/PA1010 composite coatings. By treating the surface of Al2O3 particles with a suitable bonding agent, the distribution of Al2O3 particles in matrix PA1010 is more homogeneous and the bonding state between Al2O3 particles and matrix PA1010 is better. Therefore, the Al2O3 particles in Al2O3/PA1010 composite coatings make the Al2O3/PA1010 composite coatings have bet
关键词: