Preparation and Characterization of Component Materials for Intermediate Temperature Solid Oxide Fuel Cell by Glycine-Nitrate Process
来源期刊：JOURNAL OF RARE EARTHS2006年增刊第2期
论文作者：Ma Wenhui Du Qingshan Liu Ronghui Ma Xueju Yang Bin Dai Yongnian Wang Hua
Key words：intermediate temperature solid oxide fuel cell; glycine-nitrate process; properties of materials; rare earths;
Abstract: La1-xSrxGa1-yMgyO3-δ (LSGM) electrolyte, La1-xSrxCr1-yMnyO3-δ (LSCM) anode and La1-xSrxFe1-yMnyO3-δ (LSFM) cathode materials were all synthesized by glycine-nitrate process (GNP). The microstructure and characteristics of LSGM, LSCM and LSFM were tested via X-ray diffraction(XRD), scanning electron microcopy (SEM), A C impedance and four-probe direct current techniques. XRD shows that pure perovskite phase LSGM electrolyte and electrode (LSCM anode and LSFM cathode) materials were prepared after being sintered at 1400 ℃ for 20 h and at 1000 ℃ for 5 h, respectively. The max conductivities of LSGM (ionic conductivity), LSCM (total conductivity) and LSFM (total conductivity) materials are 0.02, 10, 16 S·cm-1 in the air below 850 ℃, respectively. The conductivity of LSCM becomes smaller when the atmosphere changes from air to pure hydrogen at the same temperature and it decreases with the temperature like metal. The porous and LSGM-based LSCM anode and LSFM cathode films were prepared by screen printing method, and the sintering temperatures for them were 1300 and 1250 ℃, respectively. LSGM and electrode (LSCM and LSFM) materials have good thermal and chemical compatibility.
Ma Wenhui1，Du Qingshan1，Liu Ronghui1，Ma Xueju1，Yang Bin1，Dai Yongnian1，Wang Hua1
(1.Faculty of Materials and Metallurgical Engineering, Kunming University of Science and Technology, Kunming 650093, China;
2.National Engineering Laboratory of Vacuum Metallurgy, Kunming 650093, China)
Abstract:La1-xSrxGa1-yMgyO3-δ (LSGM) electrolyte, La1-xSrxCr1-yMnyO3-δ (LSCM) anode and La1-xSrxFe1-yMnyO3-δ (LSFM) cathode materials were all synthesized by glycine-nitrate process (GNP). The microstructure and characteristics of LSGM, LSCM and LSFM were tested via X-ray diffraction(XRD), scanning electron microcopy (SEM), A C impedance and four-probe direct current techniques. XRD shows that pure perovskite phase LSGM electrolyte and electrode (LSCM anode and LSFM cathode) materials were prepared after being sintered at 1400 ℃ for 20 h and at 1000 ℃ for 5 h, respectively. The max conductivities of LSGM (ionic conductivity), LSCM (total conductivity) and LSFM (total conductivity) materials are 0.02, 10, 16 S·cm-1 in the air below 850 ℃, respectively. The conductivity of LSCM becomes smaller when the atmosphere changes from air to pure hydrogen at the same temperature and it decreases with the temperature like metal. The porous and LSGM-based LSCM anode and LSFM cathode films were prepared by screen printing method, and the sintering temperatures for them were 1300 and 1250 ℃, respectively. LSGM and electrode (LSCM and LSFM) materials have good thermal and chemical compatibility.
Key words:intermediate temperature solid oxide fuel cell; glycine-nitrate process; properties of materials; rare earths;