Effects of V and Zr Additions on Microstructures and Mechanical Properties of Nb-Ti-Al-Base Alloys
来源期刊:稀有金属材料与工程2009年增刊第3期
论文作者:Li Zhongkui Bai Run Xia Mingxing Zheng Xin Wang Donghui
关键词:Nb-Ti-Al-base alloy; vanadium; zirconium; microstructure; mechanical properties;
摘 要:Microstructures and mechanical properties of Nb-32Ti-7Al alloys containing different V and Zr contents were investigated. The microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The alloy with V and Zr presents single phase: Nb solid solution (Nb_(ss)). Tensile testing was carried out at room temperature and 1373 K. The results show that these alloys have good ductility at room temperature. The strengths at room and high temperature increase with the addition of V and Zr, but the room temperature ductility decrease.
()
摘要:Microstructures and mechanical properties of Nb-32Ti-7Al alloys containing different V and Zr contents were investigated. The microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The alloy with V and Zr presents single phase: Nb solid solution (Nb_(ss)). Tensile testing was carried out at room temperature and 1373 K. The results show that these alloys have good ductility at room temperature. The strengths at room and high temperature increase with the addition of V and Zr, but the room temperature ductility decrease.
关键词:Nb-Ti-Al-base alloy; vanadium; zirconium; microstructure; mechanical properties;