Effects of Film Thickness and Anodizing Potential on the Characteristics of Micro-porous Structure on 316L Stainless Steel Surface
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2009年第S1期
论文作者：王玉江
文章页码：145 - 147
摘 要：A novel process for fabricating an in-situ micro-porous on 316 L stainless steel was described.Aluminum films about 0.7-1.4 m in thickness were deposited on 316 L stainless steel surface by magnetron sputtering.The films were then anodized in 0.3 M oxalic acid.Through appropriate chemical dissolution,the alumina film was removed and the underlying micro-porous 316 L with diameters ranging from 500 nm to 2.4m was obtained.The morphology of the porous 316 L surface was examined by scanning electron microscope.The results indicate that the thickness of aluminum films and the anodizing potential have a combined action on the formation of porous structure on 316 L surface.Then anodic current density could be affected evidently by the film thickness.The pores size increases obviously with the increasing of the anodizing potential,when the thickness of aluminum film was about 1.4m.
王玉江
School of Materials Science & Engineering,Harbin Institute of Technology
摘 要：A novel process for fabricating an in-situ micro-porous on 316 L stainless steel was described.Aluminum films about 0.7-1.4 m in thickness were deposited on 316 L stainless steel surface by magnetron sputtering.The films were then anodized in 0.3 M oxalic acid.Through appropriate chemical dissolution,the alumina film was removed and the underlying micro-porous 316 L with diameters ranging from 500 nm to 2.4m was obtained.The morphology of the porous 316 L surface was examined by scanning electron microscope.The results indicate that the thickness of aluminum films and the anodizing potential have a combined action on the formation of porous structure on 316 L surface.Then anodic current density could be affected evidently by the film thickness.The pores size increases obviously with the increasing of the anodizing potential,when the thickness of aluminum film was about 1.4m.
关键词：